Preparation and photocatalytic properties of dual-crystalline glass-ceramics containing NASICON-type KTi2(PO4)3 and anatase-type TiO2
Xinyu Liu,Zhiwei Luo,Chengjian Wen,Songxuan Liu,Ping Zhang,Haozhang Liang,Anxian Lu
DOI: https://doi.org/10.1016/j.jnoncrysol.2022.121661
2022-08-01
Abstract:The K2O-ZnO-TiO2-P2O5 system glasses with different components were successfully prepared by the conventional melt-quenching method. According to the results of DSC, two-step heat treatment was carried out, and NASICON-type KTi2(PO4)3 were precipitated in the glass matrix as the main crystal phase. In addition, anatase-type TiO2 crystals were also detected in some glass ceramics. The surface grain morphology of the glass-ceramics was observed by SEM, and the optical band gap was estimated by UV–vis DRS. Under the irradiation of a high-pressure mercury lamp, the photodegradation ability of the glass-ceramics to methylene blue (MB) solution was investigated. KTi2(PO4)3 and anatase phases were the reasons for the photocatalytic activity of the glass-ceramics, and the MB degradation rate can reach 55–79% after illumination for 120 min. At the same time, the glass-ceramics were separated from the solution by settling for 15 min. The results show that prepared glass-ceramics have excellent UV photocatalytic performance and can be easily separated from the aqueous medium, which has potential application in the purification of organic dye wastewater.
materials science, multidisciplinary, ceramics