Multi-response optimization of FSW process parameters of dissimilar aluminum alloys of AA2014 and AA6061 by response surface methodology (RSM)

Mehdi, Husain

DOI: https://doi.org/10.1007/s12008-023-01409-2

2023-06-27

International Journal on Interactive Design and Manufacturing

Abstract:This work aims to establish the mathematical model to predict the hardness, UTS, and % elongation of the FSW joints of AA6061 and AA2014 using RSM. The experiment was designed with three factors and three levels, resulting in 20 experimental runs. The model's adequacy was checked using analysis of variance at a 95% confidence level, and input parameters, i.e. Tool tilt angle (TTA), Tool rotational speed (TRS), and welding speed (WS), and output responses, i.e. hardness, UTS, and % strain were considered. This work perceived that TRS and WS were the most significant parameters affecting the mechanical characteristics of the weldments. The maximum UTS (235.76 MPa) and percent strain (19.35) was achieved at a TRS of 1200 rpm, a WS of 100 mm/min, and a TTA of 2°. On the other hand, the lowest UTS (136.92 MPa) and microhardness (63 HV) were observed at a WS of 70 mm/min, a TTA of 2°, and a TRS of 900 rpm. The plastic deformation observed by the stirring action of the tool, accompanied by the high temperature, leads to the DRX of grains. The grains are shattered into a refined structure due to the rotation and movement of the tool during welding. The average grain size for sample numbers 7, 10, 2, and 12 was observed as 11.56 μm, 9.86 μm, 5.63 μm, and 4.12 μm. The formation of sub-grains was found to be essential in improving the UTS of FSW joints. The sub-grains can act as obstacles to dislocation motion and enhance the material's strength and toughness. The refined grain structure observed in the stir zone of the FSW weldments of AA2014 and AA6061 at high rotational tool speeds might be attributed to the mutual effect of high temperature, DRX, and plastic deformation.