3D printed bone tissue regenerative PLA/HA scaffolds with comprehensive performance optimizations

Boqing Zhang,Ling Wang,Ping Song,Xuan Pei,Huan Sun,Lina Wu,Changchun Zhou,Kefeng Wang,Yujiang Fan,Xingdong Zhang

DOI: https://doi.org/10.1016/j.matdes.2021.109490

2021-03-01

Abstract:<p>Polylactic acid/Hydroxyapatite (PLA/HA) composite was widely studied and applied in the field of biomaterials for its good processability, bioactivity, and mechanical properties. In addition to traditional preparation methods, additive manufacturing has also been adopted to prepare PLA/HA composites with customized geometries. This work combined the comprehensive optimized PLLA (L-polylactic acid)/nano-HA (nHA) composite with the low-cost and stable Fused deposition modeling (FDM) technology to successfully prepare PLLA/nHA porous bone repair scaffolds. The results showed that PLLA/nHA composite ink satisfied the smoothness of printing, and the accuracy also met the requirements of personalized bone repair application. The high loaded nHA scaffold had suitable compressive strength was significantly higher than those of pure HA ceramic scaffold and cancellous bone. Besides, in vitro bone-like apatite formation on the surface in the degradation process and in vivo evaluations further verified its good osteogenic property. Compared with other complex and cutting-edge 3D printing technologies, this study provides a low-cost, stable, simple and fast way to realize personalized printing of bone repair scaffolds, which is undoubtedly conductive to the improvement and rapid deployment of personalized biomaterials in clinical applications.</p>

materials science, multidisciplinary

What problem does this paper attempt to address?

The main problem that this paper attempts to solve is to develop a PLA/HA scaffold for 3D - printed bone tissue regeneration with comprehensive performance optimization. Specifically, the research aims to:

1. **Prepare high - performance composite materials**: The polylactic acid (PLLA)/nano - hydroxyapatite (nHA) composite with high - loaded nHA was successfully prepared by the wet - compounding process for 3D - printing of bone repair scaffolds.

2. **Improve biological activity**: In the in - vitro degradation experiment, an apatite layer similar to bone can be formed on the surface of the scaffold, indicating its high biological activity.

3. **Optimize mechanical properties**: The scaffold with high - loaded nHA has appropriate compressive strength and shows good osteogenic properties.

4. **Achieve personalized printing**: The research provides a low - cost, stable, simple and fast method to realize 3D - printing of personalized bone repair scaffolds, which helps to improve the popularization and rapid deployment of personalized biomaterials in clinical applications.

The paper verifies these goals through the following methods and experiments:

- **Material preparation**: The PLLA/nHA composite was prepared by the wet - compounding process, and the composite filaments required for 3D - printing were prepared by the melt - extrusion method.
- **3D - printing**: The PLLA/nHA scaffolds with specific pore structures were printed using FDM technology.
- **Performance testing**: The physicochemical properties, mechanical properties, degradation behavior and biological characteristics of the scaffolds were characterized in detail.
- **In - vivo and in - vitro experiments**: The biocompatibility and bone regeneration ability of the scaffolds were evaluated through in - vitro cell experiments and in - vivo animal experiments.

Overall, this research aims to develop a high - performance scaffold suitable for bone tissue regeneration by optimizing the preparation of PLLA/nHA composites and the 3D - printing process.