Nitrogen-Doped carbon coupled FeNi3 intermetallic compound as advanced bifunctional electrocatalyst for OER, ORR and zn-air batteries
Ding Chen,Jiawei Zhu,Xueqin Mu,Ruilin Cheng,Wenqiang Li,Suli Liu,Zonghua Pu,Can Lin,Shichun Mu
DOI: https://doi.org/10.1016/j.apcatb.2020.118729
2020-07-01
Abstract:<p>Developing OER&ORR bifunctional electrocatalysts has great significance for promoting the green energy conversion and storage technologies. Herein, nitrogen doped carbon coupled FeNi<sub>3</sub> intermetallic compound (FeNi<sub>3</sub>@NC) is designed and constructed by a super facile route. Rich defects, multiple active centers and strong synergistic effect allow FeNi<sub>3</sub>@NC with superior OER&ORR performance in alkaline environments. It exhibits an ultralow overpotential (E<sub>over</sub>) of 277 mV at 10 mA/cm<sup>2</sup> for OER, and a high half-wave potential (E<sub>1/2</sub>) of 0.86 V for ORR which outperform commercial Pt/C electrocatalysts. As a result, the ΔE (ΔE = E<sub>over</sub>,OER – E<sub>1/2</sub>,ORR) value of 0.65 V largely surpasses Pt/C-IrO<sub>2</sub> noble metal benchmarks (ΔE = 0.73 V). Furthermore, density function theory calculations are performed to probe its electrocatalytic mechanism. As expected, the peak power density and energy density of FeNi<sub>3</sub>@NC based rechargeable Zn-air battery reaches 139 mW/cm<sup>2</sup> at 234 mA/cm<sup>2</sup> and 915 Wh kg<sup>-1</sup> at 10 mA/cm<sup>2</sup>, respectively, with excellent stability. Our exploration provides a guideline for synthesis of advanced bifunctional electrocatalyst.</p>
chemistry, physical,engineering, chemical, environmental