A bio-inspired multifunctional soy protein-based material: From strong underwater adhesion to 3D printing

Yue Li,Xinxin Huang,Yantao Xu,Chao Ma,Li Cai,Jieyu Zhang,Jing Luo,Jingchao Li,Jianzhang Li,Sheldon Q. Shi,Qiang Gao
DOI: https://doi.org/10.1016/j.cej.2021.133017
IF: 15.1
2022-02-01
Chemical Engineering Journal
Abstract:The use of natural plant proteins to prepare underwater bonding materials with both strong adhesion and bonding performance underwater is a great challenge. Inspired by mussels and oysters, a Soy protein isolate (SPI)-based underwater adhesive (USPI-CaO) was designed and synthesized. First, 1, 2-epoxy-9-decene (A) was grafted onto SPI to obtain ASPI with unsaturated bond by ring-opening reaction. As a natural source of catechol groups, biological urushiol (U) was then grafted onto ASPI by free-radical polymerization to obtain USPI with underwater adhesion performance. Then, calcium oxide (CaO) was mixed with USPI to obtain inorganic-organic hybrid material (USPI-CaO) with underwater curing ability. The resultant USPI-CaO showed strong underwater adhesion and bonding performance to different materials (glass, metal, PVA, acrylic, wood, hogskin, rubber, ceramic etc., respectively) in different aqueous environments (pH = 5 or 9 water, simulated seawater, organic solvent, iron solution, T = 3 ℃ to 90 ℃ water, etc., respectively). Interestingly, USPI-CaO showed good plasticity and machinability in water, demonstrating its application prospects for underwater 3D printing and underwater fine machining. USPI-CaO also exhibited good antibacterial, mildew-resistant, and fire-resistant properties. USPI-CaO can potential be applied in various fields, such as sealing and repairing underwater/wastewater, wound and hemostatic dressings, wearable electronic devices, and submerged structures.
engineering, chemical, environmental
What problem does this paper attempt to address?