Abstract:Sliver is a common but easily neglected defect in single crystal Ni-based superalloy castings.To date,there is still no unified viewpoint on its formation mechanism and generation causes.In this work,the orientation discontinuity and motion behavior of sliver defects were studied through experiments and numerical simulations.The ultrathin wedge-shaped specimen containing the grain boundary of the sliver and the matrix was prepared at the initial position of the sliver defect for the observation of equal thick-ness fringes.The discontinuity of equal thickness fringes on both sides of the grain boundary was ob-served through a transmission electron microscope,which directly confirms the abrupt change in the orientation between the sliver and matrix from the nanoscale.The crystal lattices at the smooth area and the bulging area of the grain boundary were found to have unusually different arrangements.The irregular lattice arrangement at the bulging area shows that the grain boundary has experienced high-stress deformation.Statistical results of sliver orientation deviation with a further composition analysis show the micro protuberance of the mold shell has a noticeable inductive effect on the sliver generation.Furthermore,a self-developed three-dimensional phase-field simulation model coupled with the spatial topology algorithm is established to simulate the orientation deflection behavior and orientation devia-tion threshold of fractured dendrites.The simulation results indicated that there is an upper limit of the cross-section solid fraction at the fracture position for the motion of the fractured dendrites.When the cross-section solid fraction at the fracture position is higher than this upper limit,it will be difficult to produce large deviation slivers due to the structural limitation of surrounding dendrites.This upper limit does not change with the solidification temperature gradient.

A Study of Sliver in C-Shaped Grain Selectors during Investment Casting of Single-Crystal Superalloy

Formation of Sliver Defects in Single Crystal Castings of Superalloys

Sliver defect formation in single crystal Ni-based superalloy castings

Generation Mechanism and Motion Behavior of Sliver Defect in Single Crystal Ni-based Superalloy

Grain Selection During Casting Ni-Base, Single-Crystal Superalloys with Spiral Grain Selector

Formation of Slivers in the Extended Cross‐Section Platforms of Ni‐Based Single Crystal Superalloy

A Study of Grain Selection in Two-Dimensional (2D) Grain Selectors during the Investment Casting of Single-Crystal Superalloy

Simulation of Grain Selection During Single Crystal Casting of A Ni-Base Superalloy

Numerical Study on the Formation of Spurious Grains and Freckles During the Directional Solidification of Superalloys

Simulation of grain selection during solidification of Ni base single crystal superalloy in spiral grain selector

An insight into the creep failure mechanism of sliver defect in the second-generation nickel-based single crystal superalloy CMSX-4

Numerical Simulation and Experimental Study on Spiral Grain Selector in Directional Solidification of Single Crystal Superalloy

Optimization of Grain-Selection Behavior in the Spiral Selector During Cusp-Magnetic-Field-Assisted Directional Solidification of Single-Crystal Superalloy

Numerical Simulation of Temperature Field and Grain Texture During Casting Single Crystal Superalloy DD403 with Liquid Metal Cooling

Grain Orientation Optimization Of Two-Dimensional Grain Selector During Directional Solidification Of Ni-Based Superalloys

Effects of Spiral Geometries on Grain Selection During Casting of Single Crystal Superalloys

Grain Selection in a High-Efficiency 2D Grain Selector During Casting of Single-Crystal Superalloys

Numerical Simulation of Grain Selection Behavior of Single Crystal Ni3al Based Superalloy Casting

Simulation and Experimental Study on the Directional Solidification Process of a Single Crystal Superalloy Plate Casting

Microstructural Evolution and Defect Formation in a Powder Metallurgy Nickel-Based Superalloy Processed by Selective Laser Melting

Competitive Grain Growth Mechanism in Three Dimensions During Directional Solidification of A Nickel-Based Superalloy