Excellent UV-absorbing cotton fabric with high durability and hydrophobicity based on surface-initiated ATRP of polymerizable organic UV-absorber

Saixiang Hua,Huichao Zhu,Xiao Wang,Mingyuan Wu,Qingyun Wu,Jiuyi Liu,Jianjun Yang,Jianan Zhang

DOI: https://doi.org/10.1007/s10570-022-04732-1

IF: 6.123

2022-07-15

Cellulose

Abstract:Ultraviolet (UV) protective cotton fabric is a convenient and reliable way to protect human body from sunlight. Herein, a polymerizable UV-absorber, 2-hydroxy-4-(3-methacryloxy-2-hydroxylpropoxy) benzophenone (BPMA) was prepared from the ring-opening addition reaction of 2,4-dihydroxybenzophenone (UV-0) with glycidyl methacrylate. The initiators tethered cotton fabric (CF-Br) was prepared by the immobilization of α-bromoisobutyryl groups. PBPMA grafted cotton fabric (CF-g-PBPMA) was fabricated via surface-initiated activators generated by electron transfer for atom transfer radical polymerization (SI-AGET ATRP). The results indicated that the structure of targeted polymerizable BPMA was defined, and PBPMA chains were successfully grafted from CF-Br to obtain CF-g-PBPMA. Compared with the UV protection factor (UPF) of the original cotton fabric (3.5), the UPF of CF-g-PBPMA achieved 79,630.2 at PBPMA polymerization degree of 404 due to the incorporation of 2-hydroxy benzophenone in repeating units of PBPMA. The as-prepared CF-g-PBPMA can be labeled as "Excellent UV Protection" according to the ASTM D 6603 with UPF values of above 40. Compared with the original cotton fabric, the CF-g-PBPMA displayed excellent superhydrophobicity with the water contact angle (WCA) increasing from 46° to 154° due to the increased surface roughness of cotton fabric induced by the accumulated PBPMA. After 200 washing cycles, the chemically bonded PBPMA enabled the CF-g-PBPMA outstanding durability with the WCA and UPF achieving 135° and 730.5, respectively.

materials science, textiles,polymer science, paper & wood