Abstract:Recently, the use of accelerated carbonation curing has attracted wide attention as a promising method to reduce carbon dioxide (CO2) emission and improve the mechanical properties of cement-based materials. However, the diffusion mechanism of CO2 in the matrix and the content of hydration products are the key factors that restrict the carbonation reaction rate. To understand the combined behavior of hydration and carbonation reactions, this paper investigates the influence of cement hydration induced by water-to-cement ratio (w/c) (ranging from 0.25 to 0.45) on microstructure and microhardness properties of cement paste. The experimental results demonstrated that carbonation only occurred at the surface layer of cement paste samples and carbonation efficiency was significantly influenced by greater hydration due to higher w/c. The carbonation depth of the sample with 0.45 w/c was about 6 times higher than that of sample with 0.25 w/c after 28 days of CO2 curing. XRD results revealed that calcite-type calcium carbonate is the main carbonation product and consumption of clinker phases (C2S and C3S) during the hydration enhanced the calcite precipitation in the pores of the surface layer. According to FTIR, with increasing w/c, the position of Si-O-Si stretching bond of the carbonated surface changed from Q2 to Q3, confirming the formation of amorphous silica-rich gel, along with the appearance of CO32- bonds related to calcite. In overall, the micro-mechanical analysis in this study showed that the carbonation significantly improved the surface microhardness of cement paste samples, while the refinement of capillary pores due to carbonation also decreased the negative impact of large pores formed in the matrix of cement paste prepared with high w/c.<h3 class="u-h4 u-margin-m-top u-margin-xs-bottom">Main finding</h3>Relatively high water-to-cement ratios increased the CO2 sequestration of cement paste and comparatively enhanced the porosity and microhardness at surface layer.

Strength and permeation characteristics of pervious concrete subjected to accelerated carbonation curing

Microstructure Refinement of Calcium-Sulfate-aluminate and Portland Cement (CSA-PC) Hybrids with Accelerated CO2 Curing (ACC)

Use of Carbonation Curing to Improve Mechanical Strength and Durability of Pervious Concrete

Enhanced Carbonation Curing of Cement Pastes with Dolomite Additive

Sustainable Building Material from CO2 Mineralization Slag: Aggregate for Concretes and Effect of CO2 Curing

Effects of CO2 Curing on the Properties of Pervious Concrete in Different Paste–Aggregate Ratios

Carbonation Curing of Industrial Solid Waste‐based Aerated Concretes

An overview of utilizing CO2 for accelerated carbonation treatment in the concrete industry

Effect of Isobutyl-Triethoxy-silane Penetrative Protective Agent on the Carbonation Resistance of Concrete

Microstructure refinement of calcium-sulfate-aluminate and portland cement (CSA-PC) hybrids with accelerated CO 2 curing (ACC)

Experiment Research on Property Changes of Cement-Based Materials by Accelerated Carbonation

An Overview on the Influence of Various Parameters on the Fabrication and Engineering Properties of CO2-cured Cement-Based Composites

Natural and Accelerated Carbonation of Concrete Containing Fly Ash and Ggbs after Different Initial Curing Period

Effect of concrete preconditioning method on accelerated carbonation rate

Mechanical strength and durability of mineral admixture concrete subjected to accelerated carbonation

Accelerated Carbonation of Vibro-Compacted Porous Concrete for Eco-Friendly Precast Elements

Effect of water-to-cement ratio induced hydration on the accelerated carbonation of cement pastes

Carbonation of Alkali-Activated Materials: A Review

The Carbon Absorb of Cement-Based Material in the Accelerated Carbonation Test

Accelerated Mineral Carbonation Curing of Cement Paste for CO2 Sequestration and Enhanced Properties of Blended Calcium Silicate

Superior CO<sub>2</sub> uptake and enhanced compressive strength for carbonation curing of cement-based materials via flue gas