Abstract:The aeronautical industry constantly strives for efficient technologies to facilitate hole-making in CFRP/Ti6Al4V structural components. The prime challenge in this direction is excessive tool wear because of the different engineering properties of both materials. Nanofluid minimum quantity lubrication (NF-MQL) is the latest technology to provide synergistic improvement in tool tribological properties and lubrication function during machining. In the current study, an MoS2-based NF-MQL system was applied during helical milling using a FIREX-coated tool. In-depth analysis of wear, a scanning electron microscope (SEM), and electron deposition spectroscopy (EDS) were used to evaluate workpiece elemental transfer and tool wear mechanisms. Experimental findings showed that 1% nanoparticles concentration in lubricant resulted in low tool wear of 13 μm after 10 holes. The SEM and EDS analyses depicted formation of tribo-film on the surface, resulting less severe wear and a reduced degree of adhesion. However, a low nanoparticle concentration of 0.5% resulted in 106 μm tool wear after 10 holes with slight evidence of tribo-film. Parametric analysis based on eccentricity, spindle speeds (individual for CFRP and Ti6Al4V), axial pitch, and tangential feed showed correlations with mechanical damage. An extended study of up to 200 holes showed diffusion of C element at a high rate as compared to metal elements such as W and Co. The lowest tool wear was observed using eccentricity level 1, spindle speed Ti6Al4V 1000 rpm, spindle speed CFRP 7500 rpm, tangential feed 0.01 mm/tooth, axial pitch 1.5 mm, and 1% of MoS2 nanoparticles.

What problem does this paper attempt to address?

The problem that this paper attempts to solve is the serious tool - wear problem existing in the drilling process of aerospace composite CFRP/Ti6Al4V structural parts. Specifically, due to the differences in engineering properties between CFRP (Carbon Fiber Reinforced Polymer) and Ti6Al4V (titanium alloy), tool wear is aggravated during the processing, which affects the processing efficiency and quality. To solve this problem, the paper introduced the nanofluid minimum quantity lubrication technology (NF - MQL), by using nanofluid based on molybdenum disulfide (MoS₂) to improve the tribological performance and lubrication function of the tool, thereby reducing tool wear and improving processing efficiency and surface quality. ### Background and Objectives of the Paper 1. **Background**: - In the aerospace industry, CFRP/Ti6Al4V composites are widely used because of their excellent mechanical and physical properties. - However, when processing this composite material, due to the differences in properties of the two materials, tool wear is serious, which affects the processing quality and efficiency. - The use of traditional dry cutting and a large amount of coolant has health and environmental problems, so it is necessary to find a more environmentally - friendly and effective lubrication method. 2. **Objectives**: - By introducing the nanofluid minimum quantity lubrication technology (NF - MQL), reduce tool wear and improve processing efficiency and surface quality. - Study the influence of different parameters (such as eccentricity, spindle speed, axial feed, tangential feed, etc.) on tool wear and optimize processing parameters. ### Experimental Design - **Experimental Materials**: 31 - layer 3K carbon fiber CFRP, Ti6Al4V titanium alloy plate. - **Experimental Equipment**: MCV - 600 vertical milling machine, minimum quantity lubrication system. - **Experimental Parameters**: eccentricity, spindle speed, axial feed, tangential feed, nanofluid concentration. - **Experimental Method**: Use the Taguchi method to design the experiment. A total of 36 experiments are carried out. Each experiment is divided into three steps: first process Ti6Al4V, then process CFRP, and finally verify the drilling depth. ### Main Findings - **Nanofluid Concentration**: A 1% MoS₂ nanoparticle concentration in the lubricant has the best effect, and the tool wear is the lowest (13 µm). - **Spindle Speed**: For CFRP, the tool wear is the smallest when the spindle speed is 7500 rpm; for Ti6Al4V, the tool wear is the smallest when the spindle speed is 1000 rpm. - **Axial Feed**: An axial feed of 1.5 mm has the best effect, and the tool wear is relatively low. - **Tangential Feed**: A tangential feed of 0.01 mm/tooth has the best effect, and the tool wear is the lowest. - **Comprehensive Optimization**: The optimal parameter combination is: eccentricity of 1 mm, Ti6Al4V spindle speed of 1000 rpm, CFRP spindle speed of 7500 rpm, tangential feed of 0.01 mm/tooth, axial feed of 1.5 mm, and 1% MoS₂ nanoparticle concentration. ### Conclusion By using the nanofluid minimum quantity lubrication technology (NF - MQL) based on molybdenum disulfide (MoS₂), tool wear can be significantly reduced, and processing efficiency and surface quality can be improved. The optimal combination of processing parameters is: eccentricity of 1 mm, Ti6Al4V spindle speed of 1000 rpm, CFRP spindle speed of 7500 rpm, tangential feed of 0.01 mm/tooth, axial feed of 1.5 mm, and 1% MoS₂ nanoparticle concentration. These findings provide an important reference for the efficient processing of aerospace composites.

Using Nano-Fluids Minimum Quantity Lubrication (NF-MQL) to Improve Tool Wear Characteristics for Efficient Machining of CFRP/Ti6Al4V Aeronautical Structural Composite

Tribology and machinability performance of hybrid Al2O3 -MWCNTs nanofluids-assisted MQL for milling Ti-6Al-4 V

Study on High-Speed Machining of 2219 Aluminum Utilizing Nanoparticle-Enhanced Minimum Quantity Lubrication (MQL) Technique

Machining response of Ti64 alloy under Nanofluid Minimum Quantity Lubrication (NFMQL)

Experimental investigations on surface integrity and chip morphology in hard tuning of AISI D3 steel under sustainable nanofluid-based minimum quantity lubrication

Minimum quantity lubrication machining of aeronautical materials using carbon group nanolubricant: From mechanisms to application

Evaluation of Surface Roughness, Tool Wear and Chip Morphology during Machining of Nickel-Based Alloy under Sustainable Hybrid Nanofluid-MQL Strategy

Cold Plasma and Different Nano-Lubricants Multi-Energy Field Coupling-Assisted Micro-Milling of Al-Li Alloy 2195-T8 and Flow Rate Optimization

Comparative Study of Minimum Quantity Lubrication and Dry Drilling of CFRP/titanium Stacks Using TiAlN and Diamond Coated Drills

Tool wear mechanisms in cold plasma and nano-lubricant multi-energy field coupled micro-milling of Al-Li alloy

Effects of SiO2-Al2O3-ZrO2 Tri-hybrid Nanofluids on Surface Roughness and Cutting Temperature in End Milling Process of Aluminum Alloy 6061-T6 Using Uncoated and Coated Cutting Inserts with Minimal Quantity Lubricant Method

Machining performance and sustainability analysis of Al2O3-CuO hybrid nanofluid MQL application for milling of Ti-6Al-4V

Temperature Analysis in Cubic Boron Nitrate Cutting Tool during Minimum Quantity Lubrication Turning with a Coconut-Oil-Based Nano-Cutting Fluid Using Computational Fluid Dynamics

Surface morphology assessment of CFRP transverse grinding using CNT nanofluid minimum quantity lubrication

Evaluation of new nano-cutting fluids for the processing of carbon fiber-reinforced composite materials

A Novel Approach of Applying Copper Nanoparticles in Minimum Quantity Lubrication for Milling of Ti-6Al-4V

Experimental and 3D-Deform Finite Element Analysis on Tool Wear during Turning of Al-Si-Mg Alloy

A Study on the Effects of Hybridized Metal Oxide and Carbonaceous Nano-Cutting Fluids in the End Milling of AA6082 Aluminum Alloy

Performance evaluation of nanofluid-based minimum quantity lubrication grinding of Ni-Cr alloy under the influence of CuO nanoparticles

Research on surface roughness of high-speed milling 7075-T6 aluminum alloy using nanofluid/ultrasonic atomization minimal quantity lubrication system

Tribological properties and tool wear in milling of in-situ TiB2/7075 Al composite under various cryogenic MQL conditions