Abstract:This study aims to investigate whether the combined use of thin sheet glass (FSG) and polyurethane acrylate (PUA) can enhance the mechanical properties and biocompatibility of glass ionomer cements (GICs) to improve the overall performance of commercial GICs. In this study, an innovative approach was employed by incorporating diluents and photoinitiators into PUA to develop a novel light‐curable PUA material. The PUA was then used to modify the GIC to obtain PUA‐modified GIC. Subsequently, physical and chemical methods were employed to corrode and chemically modify the glass fiber surface to acquire dried thin sheet glass (FSG). Different proportions of FSG (10%, 20%, and 30% by mass) were mixed with PUA‐GIC to obtain FSG‐PUA modified GIC. Mechanical and biocompatibility tests were conducted on regular GIC, PUA‐GIC, resin‐modified glass ionomer cement (RMGIC), and various proportions of FSG‐PUA‐GIC materials, including flexural strength, surface hardness, water absorption rate, solubility, shear strength, compressive strength (CS), in vitro cytotoxicity, as well as short‐term oral toxicity and subcutaneous implantation trials. A novel FSG‐PUA modified GIC was successfully prepared, which not only retained the excellent biocompatibility and fluoride ion release capacity of the original GIC but also significantly enhanced its mechanical strength and durability. The application of this innovative method provides a new direction for the development of dental restorative materials, particularly in addressing the shortcomings of GICs in terms of mechanical performance. The addition of FSG notably increased the flexural strength and surface hardness of GICs, especially at a 20% additive level, demonstrating superior performance compared with standard Fuji IX (F9) and slightly better than RMGIC. Water absorption rate and solubility initially decreased and then increased with an increase in FSG content, and significantly outperformed F9 and RMGIC at 10% and 20% additive levels. Shear strength and CS decreased with an increase in FSG content but remained superior to commercial groups. Material incubation with cells in vitro for 24–48 h showed no significant impact on cell viability, with cell viability exceeding 90%. Short‐term oral toxicity tests demonstrated good biocompatibility of the material, and subcutaneous implant trials did not observe any significant inflammation or pathological changes within 12 weeks of observation. The use of FSG‐PUA materials effectively enhances the mechanical properties of GIC materials, demonstrating excellent biocompatibility and significant potential as dental restorative materials. Among them, the 20% FSG‐PUA modified GICs exhibited significantly superior flexural strength, surface hardness, shear strength, water absorption, and solubility compared with F9 and slightly surpassing RMGIC, showcasing the best mechanical performance.

Fifty years of glass ionomers (GICs). Are the latest GICs suitable for restoring back teeth?

Clinical Performance of Glass Ionomer Cement in Load-Bearing Restorations: A Systematic Review

Advances of glass ionomer cement

Enhancing glass‐ionomer cements with flake‐shaped glass: A new frontier in dental restoration

A Review of Glass-Ionomer Cements for Clinical Dentistry

Longevity of Glass Ionomer Cement as a Permanent Filling Material in Primary School-Going Children

Fluoride release and uptake by glass-ionomers and related materials and its clinical effect

Consensus on glass-ionomer cement thresholds for restorative indications

Assessment of Occlusal Load Strength of Glass Ionomer Cement and Composite in Class V Cavities: An In-Vitro Study

Environmental degradation of glass-ionomer cements: A depth-sensing microindentation study

Comparative Evaluation of Mechanical Properties of Conventional Glass Ionomer Cement Incorporated with Nonfluoridated Remineralizing Agents

An Evaluation of Experimental Calcium Ion-Leachable Nanocomposite Glass Ionomer Cements

Evaluating the Mechanical Properties of Restorative Glass Ionomers Cements

Comparative evaluation of shear bond strength of three different glass ionomer cement (conventional, zirconium-reinforced and advanced glass hybrid) in primary molars: an in vitro study

The use of glass ionomer in special needs patients

In vitro compressive strength and edge stability testing of directly repaired glass-ionomer cements

Radiation-induced Root Surface Caries Restored with Glassionomer Cement Placed in Conventional and ART Cavity Preparations: Results at Two Years

Bioactivity and remineralization potential of modified glass ionomer cement: A systematic review of the impact of calcium and phosphate ion release

Effects of novel additives on the mechanical and Biological properties of glass ionomer cement: An in vitro study

Glass ionomer bone cements based on magnesium-containing bioactive glasses

Effectiveness of glass ionomer cements in the restorative treatment of radiation-related caries — a systematic review