Effect of processing parameters on the properties of transglutaminase-treated soy protein isolate films
Yan Jiang,Chuan-He Tang,Qi-Biao Wen,Lin Li,Xiao-Quan Yang
DOI: https://doi.org/10.1016/j.ifset.2006.11.002
IF: 7.104
2007-01-01
Innovative Food Science & Emerging Technologies
Abstract:The effects of processing parameters, including the applied amount of microbial transglutaminase (MTGase), the pH of film-forming solution, air-drying temperature, as well as the additional pre-incubation, on the properties of MTGase-treated soy protein isolate (SPI) films were investigated. The treatment with low concentration of MTGase (4–10 units per gram of SPI, U g−1) significantly increased the tensile strength (TS) values of SPI films, while high concentration of MTGase (over 20 U g−1) resulted in significant decrease in the TS values (P≤0.05). The elongation at break (EB) values of corresponding films gradually decreased, and the contact angle values persistently increased with the enzyme concentration. At alkaline pH range, the TS and EB values of MTGase-treated SPI films were significantly higher than that at pH 7.0 (P≤0.05). Meanwhile, the contact angle values significantly decreased with increasing pH from 7.0 to 10.0 (P≤0.05). The TS, EB and contact angle values of MTGase-treated films gradually but insignificantly decreased with increasing the air-drying temperature from 18 to 50 °C (P>0.05). The properties of MTGase-treated films were also affected by the additional pre-incubation of film-forming solutions with MTGase before casting. Furthermore, the aggregation of SPI or its components induced by MTGase has been proved to mainly account for the influence of processing parameters on the properties of SPI films (MTGase-treated). Thus, low concentration of enzyme, alkaline pH range and low air-drying temperature, at which conditions the MTGase-induced aggregation of SPI in film-forming solutions could be in some extent inhibited or delayed, might facilitate the improvement of the properties of SPI films by MTGase, especially the mechanical and surface hydrophobic properties.