Abstract:HZSM-5 zeolites with Si/Al ratios of 20, 35, 50 and 65 were prepared by the directing crystallization process of silicalite-1 seeds. The influence of Si/Al ratios on the production of benzene, toluene, xylene and naphthalene (BTXN) originated from asphaltenes catalytic pyrolysis was explored by adopting Py-GC/MS. Modified Z5-50 zeolites were prepared by various metal ions (Ni2+, Mo6+, Fe3+, and Co2+) with different loading rates (3 % (mass), 5 % (mass), 7 % (mass), and 9 % (mass)) and the physical and chemical properties of these zeolites were characterized by XRD, SEM, ICP-OES, XPS, NH3-TPD, FTIR, Py-IR and N2 adsorption-desorption isotherm. In addition, they were employed to catalyze the conversion of asphaltenes pyrolysis production to BTXN using Py-GC/MS. Results show that the highest relative content of aromatics has been obtained over HZSM-5 with Si/Al ratio of 50 (Z5-50), reaching 61.87%. Besides, the loading of Ni, Mo, Fe, and Co on Z5-50 leads to an increase of acid strength and provides new active sites. The relative content of BTXN increases by 3.17% over 3Ni-Z5, which may be ascribed to that Ni promoted the conversion of polycyclic aromatic hydrocarbons (PAHs) to monocyclic aromatics due to the cracking of aliphatic side chains of PAHs and the decrease of phenolic activation energy. While under the catalysis of 5Mo-Z5, the relative content of aromatics and BTXN augmented by 5.75% and 4.02%, respectively. In addition, the highest relative content of aromatics reaches 70.09% when the loading rate of Fe was 7 % (mass), and the relative content of BTXN increases from 25.87% to 29.42%. The results demonstrate that the active sites provided by different metal species expressed diverse effects on BTXN. Although the Brønsted/Lewis acid ratios of HZSM-5 modified by metal decreased, the acid strength and the relative content of BTXN both increased, which illustrated that there is a synergistic catalysis with the Brønsted acid sites and Lewis acid sites provided by metal species. In general, the performance of the catalyst is affected by the pore structure, acidity and metal active sites. Moreover, the possible formation mechanism of BTXN derived from asphaltenes catalytic pyrolysis was proposed on the basis of structural features and catalytic performances of a series of zeolites.

Catalytic LPG Conversion Over Fe-Ga Modified ZSM-5 Zeolite Catalysts with Different Particle Sizes: Effect of Confined-Space Zeolite and External Magnetic Field

Enhancing Methane Conversion by Modification of Zn States in Co-Reaction of MTA

Modified ZSM-5 Zeolite for Conversion of LPG to Aromatics

Preparation of Ga Isomorphic Substituted Ultrafine Nanosized ZSM-5 Zeolite and Its Catalytic Performance for MTG Reaction

Maximizing Carbon Efficiency of Petrochemical Production from Catalytic Co-Pyrolysis of Biomass and Plastics Using Gallium-Containing Mfi Zeolites

Enhanced Catalytic Performance of Methane Combustion over Zeolite-Supported Pd Catalysts with the Lanthanum

Design of novel hierarchical cage active particles and zeolite for direct conversion of syngas to gasoline fuel

Highly selective synthesis of LPG from CO2 hydrogenation over In2O3/SSZ-13 binfunctional catalyst

One-pot green synthesis of Fe-ZSM-5 zeolite containing framework heteroatoms via dry gel conversion for enhanced propylene selectivity of catalytic cracking catalyst

Direct Conversion of Syngas to Gasoline Ranged Olefins over Na Impellent Fe@NaZSM-5 Catalyst

Boosting liquid hydrocarbons selectivity from CO2 hydrogenation by facilely tailoring surface acid properties of zeolite via a modified Fischer-Tropsch synthesis

Insights into the Key Factor of Zeolite Morphology on the Selective Conversion of Syngas to Light Aromatics over a Cr2O3/ZSM-5 Catalyst

Catalytic Conversion of Methanol and Straight-Run Gasoline over Granulated Catalysts with Different Concentrations of H-Form ZSM-5 Zeolite

Efficient conversion of benzene and syngas to toluene and xylene over ZnO-ZrO2&H-ZSM-5 bifunctional catalysts

Catalytic conversion of asphaltenes to BTXN using metal-loaded modified HZSM-5

Selective Conversion of Syngas to Propane over ZnCrOx-SSZ-39 OX-ZEO Catalysts

Realizing of ZSM-5 microspheres with enhanced catalytic properties prepared from iron ore tailings via solid-phase conversion method

Simultaneous Enhancement of Aromatic Products and Catalytic Lifetime for Catalytic Re-forming of Lignite Pyrolysis Volatiles over a Self-Assembled Hierarchical Core–Shell ZSM-5@Silicalite-1 Zeolite

Catalytic Cracking of Liquefied Petroleum Gas (LPG) to Light Olefins Using Zeolite‐based Materials: Recent Advances, Trends, Challenges and Future Perspectives

Synthesis of hollow HZSM-5 zeolite-based catalysts and catalytic performance in MTA reaction

CO 2 -assisted propane dehydrogenation to aromatics over copper modified Ga-MFI catalysts