Abstract:This study investigates the role and mechanism of electrochemical dealloying (ED) to decrease the nickel ion release and improve the biocompatibility of porous NiTi alloy. The potentiostatic dealloying was performed in an acidic solution, and the effect of ED duration on the surface morphology and composition of porous NiTi alloys was studied. The results indicated that the dealloying was initially started from the edges of primary pores by the formation of TiO 2 clusters due to preferential Ni dissolution, then progressively extended to the surface and subsequently formed a fine porous structure. Accordingly, the atomistic and microstructural models for the evolution of the porous structure were proposed. The potentiodynamic polarization (PDP) and electrochemical impedance spectrometry (EIS) methods were employed to investigate the corrosion behavior of the dealloyed specimens in a Ringer’s solution. Atomic absorption spectroscopy (AAS) measurements revealed that 120 s ED treatment could decrease the number of released nickel ions during the PDP test from 4.2 ppm to <0.01 ppm. Additionally, the in-vitro cell culture and MTT assay showed that ED treatment significantly could improve the cell adhesion and proliferation on the surface of NiTi alloy due to the formation of a superficial nickel depleted layer with near superhydrophilic behavior.

Electrochemical Dealloying of Porous Niti Alloy: Porosity Evolution, Corrosion Resistance and Biocompatibility Behavior