Structural, optical and magnetic properties of Y-doped NiFe2O4 nanoparticles prepared by simple co-precipitation method

Nguyen Anh Tien,V.O. Mittova,B.V. Sladkopevtsev,Vo Quang Mai,I. Ya Mittova,Bui Xuan Vuong

DOI: https://doi.org/10.1016/j.solidstatesciences.2023.107149

IF: 3.752

2023-04-01

Solid State Sciences

Abstract:Undoped and Y-doped NiFe2O4 nanoparticles were successfully synthesized by the simple co-precipitation method without any organic gelation agent. The appropriate annealing temperature and time to obtain single-phase spinel NiFe2-xYxO4 (x = 0, 0.05, 0.1, and 0.15) is 800 °C for 1 h. The particle size measured from scanning electron microscope (SEM) and transmission electron microscope (TEM) images confirms the nanostructural character in the range of 20–40 nm. The crystallite size (D XRD = 27.54–17.43 nm) decreased while the cubic lattice parameters (a = 8.2981–8.3510 Å) increased as the Y3+ content in nickel ferrite spinel increased. Undoped and Y-doped NiFe2O4 nanoparticles have strong optical absorption in the UV (λ = 200–400 nm) and visible (λ = 400–600 nm) ranges, together with significantly lower band gap energy (E g ) compared to the NiFe2O4 materials synthesized by the sol-gel and hydrothermal methods (E g = 1.57–1.67 eV). All the undoped and Y-doped NiFe2O4 samples exhibited strong ferromagnetic behaviour with narrow magnetic hysteresis loop and high magnetization. An increase in the doped Y3+ ion in the NiFe2O4 spinel crystal lattice reduced the saturation magnetization (M s = 84.33–28.25 emu/g) while at the same time increasing the coercivity (H c = 69.74–23.46 Oe) and remanent magnetization of the obtained materials (M r = 84.33–28.25 emu/g). In this manners, Y-doped NiFe2O4 nanopowders, with a narrow band gap and strong ferromagnetic behaviour, can be used as catalysts for photochemical reactions, as well as materials for transformer cores, magnetic conductors, and gas sensors.

chemistry, physical, inorganic & nuclear,physics, condensed matter