Three-Dimensional Bamboo-Like Amorphous N/S Co-Doped Carbon Nanotubes Encapsulated with Cu Nanoparticles/Carbon Fiber Heterostructures for Boosting Electromagnetic Wave Absorbing Properties

Chengjuan Wang,Yanxiang Wang,Haotian Jiang,Xiaodan Xu,Yang Yue,Bowen Cui,Mengfan Li,Zhenhao Xu

DOI: https://doi.org/10.2139/ssrn.4123015

2022-01-01

SSRN Electronic Journal

Abstract:Highly efficient and multifunctional electromagnetic wave (EMW) absorbers which can be easily processed are desirably required. Herein, the cupric ammonia is creatively adopted as the catalyst precursor of the in-situ growth of carbon nanotubes (CNTs) onto carbon fiber (CF) during chemical vapor deposition. Typically, when prepared at 750 ℃, N/S co-doped bamboo-like amorphous CNTs/CF with three-dimensional (3D) micro-nano-heterostructure was successfully synthesized, while some Cu nanoparticles were remained in CNTs forests. The sample obtains an excellent absorbing property toward EMWs, demonstrating a minimal reflection loss of -59.28 dB at 14.1 GHz with an ultrathin thickness of 1.42 mm. Concurrently, it is over a relatively broad effective absorption bandwidth of 3.3 GHz (12.3-15.6 GHz) with 31% loading in the paraffin matrix. The satisfying attenuation performance mainly originates from the synergistic effects of continuous 3D conducting networks, abundant interfaces, sufficient defects, and well impedance matching. Moreover, the tensile strength of the CNTs/CF reaches 3.75 GPa, and all as-prepared samples could be potentially used as reinforcements into resin composites. Remarkably, a comparative facile route is provided to produce lightweight, superior and high-strength EMW absorbing materials based on CF and CNTs.