Ni foam-supported Zn-Co-Ni ternary oxide nanosheet arrays derived from MOF precursor with enhanced performances for supercapcitor and Ni-Zn battery
Daojun Zhang,Liu Yang,Minglun Wei,Caijiang Jiang,Ruyu Cui,Junjie Liu,Xinrong Chang,Bowen Ren,Jingchao Zhang,Liangliang Huang
DOI: https://doi.org/10.1039/d2nj05544a
IF: 3.3
2023-01-27
New Journal of Chemistry
Abstract:In recent years, supercapacitor and alkaline Ni-Zn battery have attracted more and more attention, due to the advantages of high energy density, excellent rate performance, low price, environmental protection and safety. In this work, ZnCoNi-MOF precursor was prepared on nickel foam (NF) by solvothermal method at first, and then the robust transition metal oxide ZnCo2O4-NiO nanosheet arrays material was formed by calcination. As a supercapacitor cathode material, the self-supported ZnCo2O4-NiO nanosheet arrays electrode exhibits a high mass specific capacitance of 196.67 mAh g−1 (1573.66 F g-1) at a current density of 1 A g−1, even when the current density is increased by 20 times, the electrode still maintains 75.5% of initial capacity. In addition, the electrode has excellent rate performance, and the retention rate can still keep 69.6% of initial capacity after 10,000 cycles, which indicates that the electrode material has excellent electrochemical performance and cycle stability. When a ZnCo2O4-NiO//Zn battery was assembled, impressively, the potential platform can be extended to 1.70 V. The ZnCo2O4-NiO//Zn battery delivers a high capacity of 191.67 mAh g−1 at 1 A g−1. After 6000 cycles at the high current density of 8 A g−1, and the capacity retention rate is 63.33%, which is promising for constructing alkaline Ni-Zn battery with long life span.
chemistry, multidisciplinary