Abstract:Developing novel proton-conducting materials is crucial to improve the energy conversion performance of proton exchange membrane fuel cells, especially under the condition of low humidity. Metal-organic frameworks (MOFs) have expressed an apparent potential in proton conduction applications due to their orderly and tunable structure. Previous studies mainly focus on the MOFs modified with homogeneous functional groups to tune the proton conductivities. In this study, an acid-base pair synergistic strategy, namely introducing the acidic and basic groups into mix-linker MOF simultaneously to obtain acid-base coexistence materials, was firstly proposed to improve the proton conduction performance at 75% RH. Herein, 10 kinds of ML-UiO-66-(A) (B)-X were synthesized and the effects of content and ratio of acid-base pairs in MOF matrix on proton-conducting properties were studied. It was found that ML-UiO-66-(NH2) (SO3H)-5:5 possessed the highest proton conduction in the ML-UiO-66 materials, with the value of 2.8 × 10−2 S cm−1 at 353 K. In addition, at 303K, 75% RH, the proton conductivity of ML-UiO-66-(NH2) (SO3H)-5:5 reached 7.4 × 10−3 S cm−1, which is three orders of magnitude higher than pristine UiO-66 (∼980 times), two orders of magnitude higher than the base-functionalized UiO-66-NH2 (∼529 times) and about 218% higher than the acid-functionalized UiO-66-SO3H at 97% RH. The results show that at relatively lower humidity 75%, ML-UiO-66-(NH2) (SO3H)-5:5 has the better proton conductivity than other UiO-66 materials at nearly 100% RH. Meanwhile, ML-UiO-66-(NH2) (SO3H)-5:5 shows high water and thermal stability under high humidity and high temperature, which ensures its application in complex environment. Performance and mechanism studies show that the strategy of introducing acid-base pair into MOF matrix may open an avenue to design novel proton-conducting materials with excellent properties.

Construction of biomimetic proton transport channels in metal-organic framework

Oriented Construction of Efficient Intrinsic Proton Transport in MOF-808 Metal-Organic Framework

Synergistic Effect Promoting Proton Transport in Metal-Organic Framework Aerogels

High Enhancement in Proton Conductivity by Incorporating Sulfonic Acids into a Zirconium-Based Metal–Organic Framework via “Click” Reaction

Constructing highly durable proton transport channels in polybenzimidazole membranes using highly stable porous carbonized metal organic frameworks

Efficient proton exchange membranes based on bifunctional metal–organic frameworks

Strategic hierarchical improvement of superprotonic conductivity in a stable metal–organic framework system

Strategically Improving The Intrinsic Proton Conductivity Of Uio-66-Nh2 By Post-Synthesis Modification

MOFs/MXene Nano-hierarchical Porous Structures for Efficient Ion Dynamics

A robust zirconium amino acid metal-organic framework for proton conduction

Superprotonic Conductivity of a Functionalized Metal-Organic Framework at Ambient Conditions.

Synergistic effect of MOF-Directed acid-base pairs for enhanced proton conduction

Superprotonic Conductivity of UiO-66 with Missing-Linker Defects in Aqua-Ammonia Vapor

Achieving High Intrinsic Proton Conductivity via Functionalization of MOF-808 by Ionic Liquid

Improving the Proton Conductivity of MOF Materials by Regulating the Pore Space

Designable Guest-Molecule Encapsulation in Metal-Organic Frameworks for Proton Conductivity.

Enhanced Proton Conduction of Imidazole Localized in One-Dimensional Ni-metal-organic Framework Nanofibers

Sulfonated Sub-1-nm Metal-Organic Framework Channels with Ultrahigh Proton Selectivity

Proton Conductive Lanthanide-Based Metal–Organic Frameworks: Synthesis Strategies, Structural Features, and Recent Progress

Proton Conductivity of Proton Exchange Membrane Synergistically Promoted by Different Functionalized Metal-Organic Frameworks.

Imidazole encapsulated in core–shell MOFs@COFs with high anhydrous proton conductivity