Abstract:New green solvent system alkali (such as NaOH and LiOH)/urea which could rapidly dissolve cellulose could be potentially used to prepare high-performance regenerated cellulose materials with low cost. Pure regenerated cellulose materials have relatively low strength inherent effects. In this work, we choose TEMPO-oxide cellulose nanofiber (CNF) and graphene oxide (GO) as fillers to prepare isotropic regenerated cellulose membrane (RCM) with significantly enhanced mechanical properties. Dynamic mechanical analyzer (DMA) test shows that RCM with content of 5 wt% CNF has the maximum enhancement value of 32.5% improvement comparing with pure RCM. And RCM with 0.4 wt% GO has the maximum improvement of 17.9%. Mechanical properties decrease with further increasing filler contents. We employ transmission electron microscopy to confirm the structure of fillers in solution and scanning electron microscopy to observe the microstructures of these RCMs. The results are consistent with DMA tests. In addition, XRD results confirm that the crystal structure of RCMs is the same with RCMs without filler. Thermogravimetric analyses results indicate that RCMs keep great thermal stability below 300 °C. Transmittance (Tr) property is carried out by UV–Vis spectroscopy. Pure RCMs and CNF/RCMs keep high transparency at the wavelength of 800 nm. Transparency of RCMs with GO decrease quickly when the content of GO increases. In conclusion, the enhancement mechanism is proposed as the addition of fillers makes up the defects in RCMs. Furthermore, CNF illustrates large aspect ratio which is beneficial for stress transfer. As for GO, polar groups on surface provide strong interaction with the matrix. This is the first time that the enhancement effects of different fillers are systematically analyzed and compared for RCMs system. Our work could benefit the selection of appropriate fillers for such green solvent system and expand its range of applications.

Preparation and optimization of porous regenerated cellulose microspheres from cellulose tetraethyl-ammonium/urea solution for adsorption of cationic methylene blue dye

Pilot-scale preparation of cellulose/carboxymethylcellulose composite fiber for methylene blue adsorption

Synthesis of Sodium Carboxymethyl Cellulose/Poly(acrylic acid) Microgels via Visible-Light-Triggered Polymerization as a Self-Sedimentary Cationic Basic Dye Adsorbent

Ionic liquid groups modified 3D porous cellulose microspheres for selective adsorption of AO7 dye

Regenerated Cellulose/polyethyleneimine Composite Aerogel for Efficient and Selective Adsorption of Anionic Dyes

Synthesis of High-Performance Sodium Carboxymethyl Cellulose-Based Adsorbent for Effective Removal of Methylene Blue and Pb (II).

High effective adsorption of organic dyes on magnetic cellulose beads entrapping activated carbon.

Easily separated and sustainable cellulose-based adsorbent using a facile two-step modification for highly efficient methylene blue removal

Amphoteric cellulose microspheres for the efficient remediation of anionic and cationic dyeing wastewater

Creation of Regenerated Cellulose Microspheres with Diameter Ranging from Micron to Millimeter for Chromatography Applications

Adsorbents prepared from epoxy-based porous materials of microcrystalline cellulose for excellent adsorption of anionic and cationic dyes

Removal of Methylene Blue Dyes from Wastewater Using Cellulose‐based Superadsorbent Hydrogels

Hierarchical Porous Cellulose/activated Carbon Composite Monolith for Efficient Adsorption of Dyes

Hemicellulose-Based Porous Hydrogel for Methylene Blue Adsorption

Preparation and Properties of Surface Imprinted Magnetic Cellulose Microsphere with Highly Selective Adsorption

Preparation of hemicellulose-based hydrogels from biomass refining industrial effluent for effective removal of methylene blue dye

High Efficient Removal of Methylene Blue Using Microcrystalline Cellulose/Polyvinyl Alcohol/Expanded Graphite 3D Porous Foam As a “green” Adsorbent

Removal Of Methylene Blue Dye From Aqueous Solution Using Modified Cellulose Hydrogel

Functionalized porous magnetic cellulose/Fe3O4 beads prepared from ionic liquid for removal of dyes from aqueous solution

Preparation of High-Performance Cellulose Composite Membranes from LiOH/urea Solvent System

Click chemistry-induced selective adsorption of cationic and anionic dyes using functionalized cellulose methacrylate hydrogels