Electrospun Shape Memory Scaffolds for Bone Tissue Engineering
Wang Chong,Wang Min
DOI: https://doi.org/10.3389/conf.fbioe.2016.01.02339
IF: 5.7
2016-01-01
Frontiers in Bioengineering and Biotechnology
Abstract:Event Abstract Back to Event Electrospun shape memory scaffolds for bone tissue engineering Chong Wang1 and Min Wang1 1 The University of Hong Kong, Department of Mechanical Engineering, Hong Kong, SAR China Introduction: Emulsion electrospinning is extensively used to make tissue engineering scaffolds with the capability of delivering bioactive agents such as growth factors [1]. Bone morphogenetic protein-2 (BMP-2) is a potent growth factor for osteogenesis. On the other hand, shape memory polymers (SMPs) have attracted great attention in tissue engineering[2]. An SMP device can be packed into a temporary shape with a much reduced size. After implantation through a narrow path, the device may recover to its larger and permanent shape upon specific stimulus. Another important issue is electrospinning of thick, 3D scaffolds. This study investigated electrospinning of a shape memory polymer, poly(D,L-lactide-co-trimethylene carbonate) P(DLLA-co-TMC), into thermo-responsive scaffolds. An auxiliary process was studied for facilitating the formation of thick scaffolds. Materials and Methods: An established procedure was used for emulsion electrospinning to fabricate rhBMP-2 encapsulated scaffolds [1]. To make w/o emulsions, rhBMP-2 (with BSA as stabilizer) in deionized water were blended with P(DLLA-co-TMC)/chloroform solution and a surfactant. Electrospinning parameters, i.e., applied voltage, working distance, solution feeding rate and electrospinning duration, were set at 10kV, 10cm, 4ml/h and 2h. During electrospinning, the fiber collector was filled with liquid nitrogen and hence ice particles were formed on collector surface, which facilitated formation of thick scaffolds continuously. Afterwards, scaffolds were freeze-dried to remove ice particles and solvent. The scaffolds were examined using SEM and TEM. In vitro release of rhBMP-2 was studied using ELISA kit assay. The shape memory effect was also evaluated. Results and Discussion: The new technique could produce thick P(DLLA-co-TMC) scaffolds incorporated with rhBMP-2. Within 2 h, scaffolds with a thickness of 4 mm were made (Fig.1a). This was attributed to the formation of ice particles between layers. SEM examination revealed multi-layered scaffolds structure and some hollow fibers were observed. The top view of scaffolds showed that scaffolds were non-woven (Fig.1b). The pore size in the scaffolds was comparable to that of conventional electrospun scaffolds. TEM results showed fibers had a core-shell structure (Fig.1c). In compression tests, when the force was applied on the cross-section of scaffolds, scaffolds exhibited compressive strength as high as 0.8-1.3MPa (Fig.2a). In vitro release experiments showed that rhBMP-2 had a fast release in the first 24 h, followed by a slow but sustained release to the 45% level by the end of 28-day test period. For shape memory, rhBMP-2/P(DLLA-co-TMC) had a high fixation ratio at room temperature and could recover to its permanent shape from the temporary shape in 1 min at 37oC (Fig.2b). When a higher temperature was applied, the scaffolds would go back to their original shape within a shorter time. Conclusion: This study showed that thick, rhBMP-2 incorporated P(DLLA-co-TMC) scaffolds with excellent shape memory ability could be made using emulsion electrospinning with the assistance of ice particles formed on the fiber collector (which was induced by liquid nitrogen inside the fiber collector). The scaffolds possessed good mechanical properties, and controlled rhBMP-2 release could be achieved with the scaffolds. References:[1] C. Wang, M. Wang, Dual-source dual-power electrospinning and characteristics of multifunctional scaffolds for bone tissue engineering, J Mater Sci Mater Med, 2012, 23:2381-97.[2] A. Lendlein, et al. Shape-memory polymers as a technology platform for biomedical applications, Expert Review of Medical Devices 7, 357-379, 2010 Keywords: growth factor, nanofiber, Scaffold, Smart material Conference: 10th World Biomaterials Congress, Montréal, Canada, 17 May - 22 May, 2016. Presentation Type: Poster Topic: Biomaterials in constructing tissue substitutes Citation: Wang C and Wang M (2016). Electrospun shape memory scaffolds for bone tissue engineering. Front. Bioeng. Biotechnol. Conference Abstract: 10th World Biomaterials Congress. doi: 10.3389/conf.FBIOE.2016.01.02339 Copyright: The abstracts in this collection have not been subject to any Frontiers peer review or checks, and are not endorsed by Frontiers. They are made available through the Frontiers publishing platform as a service to conference organizers and presenters. The copyright in the individual abstracts is owned by the author of each abstract or his/her employer unless otherwise stated. Each abstract, as well as the collection of abstracts, are published under a Creative Commons CC-BY 4.0 (attribution) licence (https://creativecommons.org/licenses/by/4.0/) and may thus be reproduced, translated, adapted and be the subject of derivative works provided the authors and Frontiers are attributed. For Frontiers’ terms and conditions please see https://www.frontiersin.org/legal/terms-and-conditions. Received: 27 Mar 2016; Published Online: 30 Mar 2016. Login Required This action requires you to be registered with Frontiers and logged in. To register or login click here. Abstract Info Abstract The Authors in Frontiers Chong Wang Min Wang Google Chong Wang Min Wang Google Scholar Chong Wang Min Wang PubMed Chong Wang Min Wang Related Article in Frontiers Google Scholar PubMed Abstract Close Back to top Javascript is disabled. Please enable Javascript in your browser settings in order to see all the content on this page.