Preventive dental erosion with silver diamine fluoride: an in vitro study
Darren Dhananthat Chawhuaveang,May Lei Mei,Chun Hung Chu,Ollie Yiru Yu
DOI: https://doi.org/10.1016/j.jdent.2024.105022
IF: 4.991
2024-04-26
Journal of Dentistry
Abstract:Objectives To evaluate the erosion preventive effect of 38% silver diamine fluoride (SDF) solution in enamel and dentin of human permanent teeth. Methods Ninety enamel and ninety dentin blocks were prepared from permanent molars and allocated into three groups. Gp-SDF received a one-off application of 38% SDF solution. Gp-SNF received a one-off application of a solution containing 800ppm stannous chloride and 500ppm fluoride. Gp-DW received a one-off application of deionized water. The blocks were submitted to acid challenge at pH 3.2, 2 minutes, 5 times/day for 7 days. All blocks were immersed in human saliva between cycles for one hour. The crystal characteristics, percentage of surface microhardness loss (%SMHL), surface loss, and elemental analysis and surface morphology were examined by X-ray diffraction (XRD), microhardness test, non-contact profilometry, and energy-dispersive X-ray spectroscopy (EDS) and scanning electron microscopy (SEM), respectively. Data of %SMHL and surface loss were analyzed by one-way ANOVA. Results XRD spectra revealed that fluorapatite and silver compounds formed in Gp-SDF, while fluorapatite and stannous compounds formed in Gp-SNF. Gp-DW presented only hydroxyapatite. The median (interquartile range) of %SMHL in Gp-SDF, Gp-SNF and Gp-DW were 27.86(3.66), 43.41(2.45), and 46.40(3.54) in enamel ( p< 0.001), and 14.21(1.57), 27.99(1.95), and 33.18(1.73) in dentin, respectively ( p <0.001). The mean (standard deviation, μm) of surface loss of Gp-SDF, Gp-SNF, and Gp-DW were 2.81(0.59), 4.28(0.67), and 4.63(0.64) in enamel ( p <0.001) and 4.13(0.69), 6.04(0.61), and 7.72(0.66) in dentin, respectively ( p <0.001). SEM images exhibited less enamel corruption and more dentinal tubular occlusion in Gp-SDF compared to Gp-SNF and Gp-DW. EDS analysis showed silver was detected in Gp-SDF while stannous was detected in the dentin block of Gp-SNF. Conclusion 38% SDF yielded superior results in protecting enamel and dentin blocks from dental erosion compared to SNF and DW. Clinical significance Topical application of 38% SDF is effective in preventing dental erosion in human enamel and dentin.
dentistry, oral surgery & medicine