Abstract:Background: The use of acellular hydrogels to repair osteochondral defects requires cells to first invade the biomaterial and then to deposit extracellular matrix for tissue regeneration. Due to the diverse physicochemical properties of engineered hydrogels, the specific properties that allow or even improve the behaviour of cells are not yet clear. The aim of this study was to investigate the influence of various physicochemical properties of hydrogels on cell migration and related tissue formation using in vitro, ex vivo and in vivo models. Methods: Three hydrogel platforms were used in the study: Gelatine methacryloyl (GelMA) (5% wt), norbornene hyaluronic acid (norHA) (2% wt) and tyramine functionalised hyaluronic acid (THA) (2.5% wt). GelMA was modified to vary the degree of functionalisation (DoF 50% and 80%), norHA was used with varied degradability via a matrix metalloproteinase (MMP) degradable crosslinker and THA was used with the addition of collagen fibrils. The migration of human mesenchymal stromal cells (hMSC) in hydrogels was studied in vitro using a 3D spheroid migration assay over 48h. In addition, chondrocyte migration within and around hydrogels was investigated in an ex vivo bovine cartilage ring model (three weeks). Finally, tissue repair within osteochondral defects was studied in a semi-orthotopic in vivo mouse model (six weeks). Results: A lower DoF of GelMA did not affect cell migration in vitro (p = 0.390) and led to a higher migration score ex vivo (p < 0.001). The introduction of a MMP degradable crosslinker in norHA hydrogels did not improve cell infiltration in vitro or in vivo. The addition of collagen to THA resulted in greater hMSC migration in vitro (p = 0.031) and ex vivo (p < 0.001). Hydrogels that exhibited more cell migration in vitro or ex vivo also showed more tissue formation in the osteochondral defects in vivo, except for the norHA group. Whereas norHA with a degradable crosslinker did not improve cell migration in vitro or ex vivo, it did significantly increase tissue formation in vivo compared to the non-degradable crosslinker (p < 0.001). Conclusion: The modification of hydrogels by adapting DoF, use of a degradable crosslinker or including fibrillar collagen can control and improve cell migration and tissue formation for osteochondral defect repair. This study also emphasizes the importance of performing both in vitro and in vivo testing of biomaterials, as, depending on the material, the results might be affected by the model used.The translational potential of this article: This article highlights the potential of using acellular hydrogels to repair osteochondral defects, which are common injuries in orthopaedics. The study provides a deeper understanding of how to modify the properties of hydrogels to control cell migration and tissue formation for osteochondral defect repair. The results of this article also highlight that the choice of the used laboratory model can affect the outcome. Testing hydrogels in different models is thus advised for successful translation of laboratory results to the clinical application.

The degradation of gelatin/alginate/fibrin hydrogels is cell type dependent and can be modulated by targeting fibrinolysis

Controlling fibroblast fibrinolytic activity allows for the bio-engineering of stable connective tissue equivalents

Gelatin Methacrylate (GelMA)-Based Hydrogels for Cell Transplantation: an Effective Strategy for Tissue Engineering

Mechanically Resilient, Injectable, and Bioadhesive Supramolecular Gelatin Hydrogels Crosslinked by Weak Host-Guest Interactions Assist Cell Infiltration and in Situ Tissue Regeneration

Fibrin in Tissue Engineering

Fibrin Hydrogels Reinforced by Reactive Microgels for Stimulus‐Triggered Drug Administration

Fabrication and Physical and Biological Properties of Fibrin Gel Derived from Human Plasma.

Development of Human-Derived Photocrosslinkable Gelatin Hydrogels for Tissue Engineering

Enzymatically degradable alginate/gelatin bioink promotes cellular behavior and degradation in vitro and in vivo

Optimizing Peptide Crosslinks for Cell-Responsive Hydrogels

Fibrin Gel as an Injectable Biodegradable Scaffold and Cell Carrier for Tissue Engineering

Immobilization of Gelatin on Fibers for Tissue Engineering Applications: A Comparative Study of Three Aliphatic Polyesters

Enzymatic Insitu Crosslinking Can Improve Hydrogel Stability While Maintaining Matrix Stiffness

Modulating design parameters to drive cell invasion into hydrogels for osteochondral tissue formation

FITC-Dextran Release from Cell-Embedded Fibrin Hydrogels

Anisotropic Hydrogel Degradation Enhances 3D Collective Cell Alignment, Mechanotransduction and Osteogenic Differentiation

Fibroin/collagen hybrid hydrogels with crosslinking method: preparation, properties, and cytocompatibility.

Design of Alginate/Gelatin Hydrogels for Biomedical Applications: Fine-Tuning Osteogenesis in Dental Pulp Stem Cells While Preserving Other Cell Behaviors

Modular Enzymatically Crosslinked Protein Polymer Hydrogels For In Situ Gelation

Water-Insoluble, Thermostable, Crosslinked Gelatin Matrix for Soft Tissue Implant Development

3D cell entrapment in crosslinked thiolated gelatin-poly(ethylene glycol) diacrylate hydrogels