Abstract:TiO2 nanoparticles were synthesized using low‐temperature hydrothermal methods. A 1 M TiO2 sample was mixed with 50 mL of CH3COOH in a 500‐mL beaker using TiO2 as a precursor. The solution was then stirred at room temperature using a Remi digital high‐speed stirrer. Following the addition of 50 mL of distilled water, the solution was stirred for an hour. The pH level of the mixture was regulated by adding NaOH solution. In the process of dye degradation, first‐order kinetics is involved. The absorption values of ZnS nanoparticles and TiO2‐doped ZnS nanocomposites were determined by analyzing UV–Vis spectra at different time points. At the initial time point (t = 0), 617 nm was observed to be the point of maximum absorption. Dopants cause slight shifts in maximum wavelengths due to their presence. In the presence of visible light, pure TiO2 and TiO2‐doped ZnS nanocomposites are shown to be able to degrade MG dye through a photocatalytic mechanism. After 80 min, pure ZnS nanocomposites and TiO2‐doped ZnS nanocomposites degraded aqueous samples with degradation efficiencies of ~54% and ~88%, respectively, demonstrating their photocatalytic capabilities. The titanium dioxide (TiO2) nanoparticles were prepared by hydrothermal methods at ambient temperature. Based on XRD analysis, the average crystallite size of pure TiO2 nanoparticles and those doped with ZnS was calculated to be 58 and 54 nm, respectively. At an angle of 25.4°, the prominent peak observed at the (101) plane of TiO2 was confirmed. As can be seen from the collection of peaks, the TiO2 formed has an anatase‐type tetragonal crystal structure. A strain of −6.4541 × 10−4 and a grain size of 33 nm can be seen in the W–H plot for TiO2 nanoparticles. For doped ZnS nanoparticles, on the other hand, the values are 1.9448 × 10−4 and 47 nm. In our study, we found that doped nanoparticles were average grain size 134 nm, while pure nanoparticles were average grain size 146 nm. Doping reduces the size of the nanomaterial, which means that the TiO2 molecules form nanoclusters on their surfaces, which can lead to a larger grain size for a pure nanoparticle than for a doped nanoparticle. A wide range of functional groups and their associated bonds were investigated using FTIR spectra in synthesized nanomaterials. TiOTi bonds are subjected to a strong stretching vibration, which is confirmed by the absorption peaks from 450 cm−1 to 800 cm−1. The PL spectra for pure TiO2‐ and ZnS‐doped TiO2 containing nanocomposites of ZnS emit ultraviolet light at wavelengths of 362 and 379 nm in the UV region. Pure and doped samples with optical bandgap energies of ~3.04 and ~3.8 eV corresponding to anatase phases were near ~3.18 eV in Tauc plots. Since the TiO2‐doped ZnS heterojunction migrates photoexcited holes toward the interface, while electrons migrate toward the bulk, this results in photoexcited holes migrating toward the interface. To calculate the specific capacitance of the synthesized materials, cyclic voltammetry with pure ZnS and those with ZnS‐doped had specific capacitance values of 144.91 F/g and 120.11 F/g, respectively. The catalysts used were ZnS nanocomposite doped with TiO2 in addition to pure TiO2 nanoparticles. The degradation of dye within 80 min after sunlight exposure was monitored with a UV–Vis spectrophotometer at 20‐min intervals. ZnS nanoparticles doped with TiO2 display 87.8% greater efficiency than pure nanoparticles. Doped TiO2 nanocomposite degrades at an 87.8% rate, whereas pure TiO2 degrades at ~54%, indicating that the dopants enhance photocatalysis.

Photocatalytic degradation of direct red 80 using ZnO/ZnTiO3/Zn2Ti3O8 ternary nanocomposite

Photodegradation of Rhodamine B on Sulfur Doped ZnO/TiO2 Nanocomposite Photocatalyst under Visible‐light Irradiation

Ternary System of ZnO Nanorods/reduced Graphene Oxide/cuins2 Quantum Dots for Enhanced Photocatalytic Performance

Preparation of Er3+:YAlO3/Fe-doped TiO2–ZnO and its application in photocatalytic degradation of dyes under solar light irradiation

Preparation, Characterization of ZnTiO3/ZnO Composite Materials and Their Photocatalytic Performance

Mechanistic insights into the selective photocatalytic degradation of dyes over TiO2/ZSM-11

The investigation of sonocatalytic activity of Er3+:YAlO3/TiO2-ZnO composite in azo dyes degradation.

TiO2 nanotube/ZnIn2S4 nanoflower composite with step-scheme heterojunction for efficient photocatalytic H2O2 production and organic dye degradation

Electrochemical Applications Reveal Enhanced Photocatalytic Performance of TiO2‐Doped ZnS Nanocomposites

Preparation and Enhanced Visible-Light Photoelectrocatalytic Activity of Ternary TiO2ZnO/RGO Nanocomposites

A High-Efficiency TiO2/ZnO Nano-Film with Surface Oxygen Vacancies for Dye Degradation

Metal organic framework-derived C-doped ZnO/TiO2 nanocomposite catalysts for enhanced photodegradation of Rhodamine B

Photocatalytic degradation of an anionic dye in aqueous solution by visible light responsive zinc oxide-termite hill composite

ZnCDs/ZnO@ZIF-8 Zeolite Composites for the Photocatalytic Degradation of Tetracycline

Fabrication of Zn-Ti layered double oxide nanosheets with ZnO/ZnTiO3 heterojunction for enhanced photocatalytic degradation of MO, RhB and MB

A novel photocatalytic degradation of mixed dye through chemically synthesized ZnO/Fe2O3 nanocomposite

Enhancing Performance of Organic Pollutant Degradation via Building Heterojunctions with ZnO Nanowires and Na Doped Conjugated 2,4,6-Triaminopyrimidin-g-C3N4

ZnO-Bi2O3 Heterostructured Composite for the Photocatalytic Degradation of Orange 16 Reactive Dye: Synergistic Effect of UV Irradiation and Hydrogen Peroxide

Photocatalytic degradation of Indigo Carmine using aluminum-doped titanium dioxide/zinc ferrite nanocomposite under visible light

Photocatalytic degradation of tetracycline using surface defective black TiO2-ZnO heterojunction photocatalyst under visible light

Photocatalytic performance of nano-ZnTiO3 decorated with Ag/AgCl nanoparticles for degradation of the organic dyes