Ultrahigh rate and durable sodium-ion storage at a wide potential window via lanthanide doping and perovskite surface decoration on layered manganese oxides
Fang Xia,Da Tie,Jing Wang,Haili Song,Wen Wen,Xiangxi Ye,Jinsong Wu,Yanglong Hou,Xionggang Lu,Yufeng Zhao
DOI: https://doi.org/10.1016/j.ensm.2021.07.020
IF: 20.4
2021-11-01
Energy Storage Materials
Abstract:P2-type layered manganese oxides are recognized as one of the most compelling cathode candidates for sodium-ion batteries, but these materials suffer from the intrinsic structural Jahn-Teller distortion and oxygen loss, which causes limited rate capability and long-cycle fading under a wide potential window. Here we demonstrate a new approach to realize a simultaneous enhancement on both rate performance and long-term duration over a wide potential window through dilute La lattice doping and perovskite surface modification. We reveal for the first time through both DFT calculations and experimental results, that the La-doping and perovskite LCM surface decoration can efficiently suppress oxygen loss by providing O 2p holes and oxygen vacancies, and meanwhile enhance the electronic and ionic conductivity. The as achieved LNCM/LCM (LaNa0.06Co0.06Mn0.88O3/ Na0.56Co0.17Mn0.8La0.03O2) demonstrates a record high rate performance of 20C (1C=180 mA g−1) and outstanding cycling performance of 300 cycles (70% capacity retention) at a wide potential range (1.5-4.4V), which outperform the state-of-the-art Mn-based layered oxides. We confirm the reversible solid solution reaction during the charge/discharge process using the operando synchrotron XRD analysis. This work demonstrates an applicable approach to realize significant improvement on both rate capability and cycle stability without sacrificing the potential window.The various electrochemical tests of NCM and LNCM/LCM electrodes were evaluated in a Na half-cell system at room temperature. The initial charge/discharge profiles of LNCM/LCM measured at 0.1C (1C = 180 mA g−1) in the potential range of 1.5-4.4V are shown in Figure 3a. The capacity of the first charge/discharge is 103 and 154 mAh g−1, corresponding to 0.41 Na+ extraction and 0.6 Na+ insertion respectively. The rate performance of all the samples was tested at the various rate ranging from 0.1C to 20 C in the voltage range of 1.5-4.4 V. The highest initial specific capacity of 166 mAh g−1 is achieved for NCM at 0.1C (Figure S9), which is 154 mAh g−1 for the LNCM/LCM The relatively lower initial capacity could be attributed to that the LCM nanoislands cannot accommodate Na ions. On the contrary, the rate performance of LNCM/LCM is significantly enhanced, with specific capacity retaining 71 mAh g−1 even at 20 C (Figure 3i). To further verify the rate performance of LNCM/LCM, we performed a discharge test on the material with fixed 0.5C for charging, and then discharged at various rates, the material achieved a characteristic capacity of 165 mAh g−1 at 0.1C, it also delivered an excellent discharge performance: 100 mAh g−1 at 10 C and 81 mAh g−1 at 20 C (Figure S10). The cycling stability and the coulombic efficiency are displayed in Figure 3k, and the capacity is still maintained at 86 mAh g−1 at 0.5C after 300 cycles, demonstrating capacity retention of 70%, and the coulombic efficiency is close to 100%. A comparison of the rate and cycling performance for the related materials published recently is conducted as listed in Table S8. It can be seen, for those systems with +3 and +4 mixed manganese valences, they usually demonstrate a capacity beyond the theoretical value, but suffer from serious degradation upon cycling caused due to the Jahn-Teller effect. The other samples with +4 manganese demonstrate fewer phase transitions with enhanced cycling stability, but their capacity is limited. The unique structural design enables us as-prepared LNCM/LCM to simultaneously achieve high specific capacity, good rate capacity and excellent cycling stability, outperforming most state-of-art work in literature.To understand the electrochemical reaction mechanism of the material, we conducted the cyclic voltammetry (CV) test for the half-cell. As illustrated in Figure 3b, the CV curves at a scan rate of 0.1 mV s−1 of LNCM/NCM show three potential plateaus at 2.08/2.59 V, 3.41/3.52 V, and 4.34 V. The redox peaks at 3-4 V are due to the electrochemical reaction of Co3+ and Co4+, and the peaks at low potential (below 3.0 V vs Na/Na+) could be mainly assigned to the redox reactions of Mn3+/Mn4+. No new peaks are found on the curves of LNCM/LCM after the 1st curve, indicating that LCM and the La3+ in P2-phase do not participate in the charge-discharge reaction. The peaks of LNCM/LCM loaded at 2-2.3V and 4-4.4V on the first cycle are a bit different from that of later most likely due to a small distortion (P2-OP4), whi -Abstract Truncated-
materials science, multidisciplinary,chemistry, physical,nanoscience & nanotechnology