An USAXS-SAXS study of nano-TATB under uniaxial die pressures
Yan Zhou,Jing Shi,Xiu-hong Li,Feng Tian,Mark Julian Henderson,László Almásy,Qiang Tian
DOI: https://doi.org/10.1016/j.enmf.2023.03.002
2023-03-11
Energetic Materials Frontiers
Abstract:Highlights • The combination of ultra-small-angle and small-angle X-ray scattering (USAXS-SAXS) is proved to be effective in characterizing the hierarchical void structure of TATB under compression. • The analysis based on the Guinier-Porod model indicates that the intergranular voids are sensitive to low pressures ( 15 kN). • Scattering data implies that nano-TATB responds to the increase in the applied pressure follows in the sequence of the flow, fracturing, and plastic deformation of the TATB granules. The microstructure of a compressed explosive solid is closely related to its shock sensitivity and mechanical properties. In this study, ultra-small-angle and small-angle X-ray scattering (USAXS and SAXS) techniques were combined to explore the hierarchical microstructure of die-pressed 2,4,6-trinitro-1,3,5-benzenetriamine (TATB) discs obtained from nanostructured TATB (nano-TATB) powder as the precursor. Using the Guinier-Porod model, the pseudo-invariants, and Porod's law, this study analyzed the microstructures of the materials on a nanometer scale to track the changes in void size, porosity, and interfacial area, which reflected the response of TATB under applied pressures of 1, 2, 5, 10, 15 kN and 30 kN. Results show that there existed three populations of voids in the measured q range. The intergranular voids with sizes of tens of nanometers were sensitive to low pressures ( 15 kN), as indicated by the decrease in the volume fractal dimension. Porosities of the voids with sizes of 1–900 nm, which were determined by the pseudo-invariants obtained from the scattering data, decreased from 6% to 1% as the pressures increased from 1 kN to 30 kN. The response of these structural parameters to external pressures implies that the main densification mechanisms under die compression include the flow, fracturing, and plastic deformation of the TATB granules. This study provides a direct insight into the structural evolution of TATB during compression. Graphical abstract Ultra-small-angle and small-angle X-ray scattering (USAXS-SAXS) techniques were employed to investigate the hierarchical microstructure of uniaxially die-pressed TATB discs. To determine the structural evolution of the samples under the applied pressures (1, 2, 5, 10, 15 kN and 30 kN), this study analyzed the void size, porosity, and interfacial area on a nanometer scale using the Guinier-Porod model, the scattering pseudo-invariants, and Porod's law. Download : Download high-res image (188KB) Download : Download full-size image