Abstract:Cr-doped ZnAl mixed oxide catalysts (Zn0.75CrAl-x-c) were obtained via calcining the Zn0.75CrAl-x hydrotalcite precursors and were applied in the selective oxidation of 5-hydroxymethylfurfural (5-HMF) to 2,5-furandicarboxylic acid (FDCA). Cr doping significantly enhanced the catalytic activity. A 95.1% 5-HMF conversion with an 88.1% FDCA selectivity was achieved over the Zn0.75CrAl-6-c catalyst at 130 °C under 0.6 MPa oxygen for 4 h. The good performance was associated with the high specific surface area and high oxygen vacancy concentration. Moreover, the Zn0.75CrAl-6-c catalyst was used for five cycles without a significant activity loss indicating excellent stability.
What problem does this paper attempt to address?
The problem that this paper attempts to solve is to develop an efficient, stable and low - cost non - precious metal catalyst for the selective oxidation of 5 - hydroxymethylfurfural (5 - HMF) to prepare 2,5 - furandicarboxylic acid (FDCA). Specifically, the researchers prepared a zinc - chromium - aluminum mixed - oxide catalyst (Zn0.75CrAl - x - c) by calcining a hydrotalcite - like precursor and applied it to the selective oxidation reaction from 5 - HMF to FDCA. The main goal of the study was to improve the conversion rate of 5 - HMF and the selectivity of FDCA while ensuring that the catalyst has good recyclability.
### Research Background
1. **Importance of Biomass Resources**:
- Biomass resources such as lignocellulosic biomass have been widely studied for the production of high - value - added chemicals and fuels in order to reduce dependence on fossil resources, lower energy consumption and cost, and at the same time reduce environmental burdens.
2. **Application Prospects of FDCA**:
- FDCA is one of the 12 high - value chemicals derived from biomass and can be used as a renewable substitute for terephthalic acid in the production of plastics and medical anesthetics.
3. **Challenges from 5 - HMF to FDCA**:
- The formation of by - products is a major challenge in the process of selective oxidation of 5 - HMF to generate FDCA. Currently, methods for achieving efficient catalytic conversion include thermal catalysis, electrocatalysis and photocatalysis.
4. **Limitations of Existing Catalysts**:
- Although homogeneous catalysts have high activity and selectivity, they are difficult to recover and cause environmental pollution.
- Although precious - metal catalysts perform well under mild conditions, they require strong - base additives and are costly.
- Although non - precious - metal catalysts are cost - effective, there are still some deficiencies in catalyst preparation, reaction steps and reaction conditions.
### Research Methods
1. **Catalyst Preparation**:
- A zinc - chromium - aluminum hydrotalcite - like precursor was prepared by the co - precipitation method and then calcined at 460 °C for 6 hours to obtain the mixed - oxide catalyst Zn0.75CrAl - x - c.
2. **Catalyst Characterization**:
- The catalyst was characterized by X - ray diffraction (XRD), specific surface area analysis (BET), scanning electron microscopy (SEM) and X - ray photoelectron spectroscopy (XPS).
3. **Catalytic Performance Testing**:
- The catalytic reaction was carried out in a 150 mL stainless - steel autoclave under the following reaction conditions: 1 mmol 5 - HMF, 50 mg catalyst, 50 mg Na2CO3, 25 mL DMF, 130 °C, 0.6 MPa O2, and stirred at 500 rpm for 4 hours.
### Main Results
1. **Catalyst Performance**:
- The Zn0.75CrAl - 6 - c catalyst achieved a 95.1% conversion rate of 5 - HMF and an 88.1% selectivity of FDCA under the conditions of 130 °C and 0.6 MPa O2.
2. **Catalyst Stability**:
- After five cycles of use, the catalytic activity of the Zn0.75CrAl - 6 - c catalyst did not decrease significantly, showing good stability.
3. **Reaction Mechanism**:
- Through XPS analysis, it was found that there are three oxygen species (lattice oxygen, oxygen vacancies and adsorbed oxygen) on the catalyst surface. Among them, oxygen vacancies help to improve the catalytic activity and promote the oxygen supplementation on the catalyst surface. During the reaction, Cr6+ and lattice oxygen are reduced to Cr3+ and oxygen vacancies, which is in line with the Mars - van Krevelen mechanism.
### Conclusion
This study successfully prepared an efficient non - precious - metal catalyst Zn0.75CrAl - 6 - c for the selective oxidation of 5 - HMF to prepare FDCA. This catalyst not only exhibits excellent catalytic performance under mild conditions but also has good recyclability and is expected to be widely used in the production of biomass - derived chemicals.