Abstract:Microwave dielectric ceramics are vital for filters, dielectric resonators, and dielectric antennas in the 5G era. It was found that the (Cu1/3Nb2/3)4+ substitution can effectively adjust the TCF (temperature coefficient of resonant frequency) of Li2TiO3 and simultaneously increase its Q × f (Q and f denote the quality factor and the resonant frequency, respectively) value. Notably, excellent microwave dielectric properties (εr (permittivity) ≈ 18.3, Q × f ≈ 77,840 GHz, and TCF ≈ +9.8 ppm/°C) were achieved in the Li2Ti0.8(Cu1/3Nb2/3)0.2O3 (LTCN0.2) ceramic sintered at 1140 °C. Additionally, the sintering temperature of LTCN0.2 was reduced to 860 °C by the addition of 3 wt % H3BO3, exhibiting superior microwave dielectric properties (εr ≈ 21.0, Q × f ≈ 51,940 GHz, and TCF ≈ 1.4 ppm/°C) and being chemically compatible with silver. Moreover, LTCN0.2 + 3 wt % H3BO3 ceramics were designed as a patch antenna and a dielectric resonator antenna, both of which showed high simulated radiation efficiencies (88.4 and 93%) and gains (4.1 and 4.03 dBi) at the center frequencies (2.49 and 10.19 GHz). The LTCN0.2 + 3 wt % H3BO3 materials have promising future application for either 5G mobile communication devices and/or in low-temperature co-fired ceramic technology owing to their high Q, low sintering temperature, small density, and good temperature stability.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsami.0c18836?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsami.0c18836</a>.Refined lattice parameters of LTCNx (0 ≤ x ≤ 0.4) ceramics (Table S1), Raman spectra of LTCNx (0 ≤ x ≤ 0.4) ceramics (Figure S1), SEM images and densities of the LTCNx (0 ≤ x ≤ 0.4) specimens (Figure S2), phonon parameters achieved from the fitting of the infrared reflectivity spectra of the LTCN0.2 specimen (Table S2), phonon parameters achieved from the fitting of the infrared reflectivity spectra of the LTCN0.2 + 3 wt % H3BO3 ceramic (Table S3), and optimized parameters of the proposed patch antenna (Table S4) (<a class="ext-link" href="/doi/suppl/10.1021/acsami.0c18836/suppl_file/am0c18836_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

All-ceramic array patch for 5G signal enhancement based on B-site substituted zinc-cobalt molybdate low temperature co-fired ceramics

Low-temperature Co-Fired Ceramics with High Thermal Expansion and Reliability for Millimeter-Wave Antennas

5G array antenna substrate for electromagnetic beam splitting via cobalt-substituted zinc molybdate low temperature co-fired ceramics

Polarization-dependent multichannel transmission of 5 G signals based on Zn0.91(Li0.5Bi0.5)0.09MoO4 low-temperature co-fired ceramics

Polarization-dependent Multichannel Transmission of 5G Signals Based on Zn0.91(Li0.5Bi0.5)0.09MoO4 Low-Temperature Co-Fired Ceramics

Design and fabrication of a C-band patch antenna using novel low permittivity SrGa2Si2O8 microwave dielectric ceramic

Co-substituted CuO–ZrO2–Nb2O5 composite ceramics with low-temperature sintering and low-loss for high-performance patch antenna

Antenna Array Design Based on Low-Temperature Co-Fired Ceramics

Design of a High-Efficiency and -Gain Antenna Using Novel Low-Loss, Temperature-Stable Li 2 Ti 1 – x (Cu 1/3 Nb 2/3 ) x O 3 Microwave Dielectric Ceramics

Zn2+-Enhanced Lithium Magnesium Molybdate Ultralow Temperature Cofired Ceramics for Terahertz Wavefront Modulation Applications.

Low permittivity cordierite-based microwave dielectric ceramics for 5G/6G telecommunications

Design Of A High-Efficiency And -Gain Antenna Using Novel Low-Loss, Temperature-Stable Li2ti1-(X) (Cu1/3nb2/3)(X)O-3 Microwave Dielectric Ceramics

5G microstrip patch antenna and microwave dielectric properties of 4 mol%LiF–MgO–xwt%MTiO3 (M = Ca, Sr) composite ceramics

Nickel-modified zinc molybdate low temperature co-fired ceramics for two-dimensional beam splitting of array antenna in X-band

Microwave Dielectric Properties of Mg1.8R0.2Al4Si5O18 (R = Mg, Ca, Sr, Ba, Mn, Co, Ni, Cu, Zn) Cordierite Ceramics and Their Application for 5G Microstrip Patch Antenna

Cold sintering optimized LiF microwave dielectric ceramics for the development of dielectric resonator antennas at 5G millimeter-wave band

Microwave dielectric properties of ultra-low temperature sintered Co1−xMgxMoO4 (x = 0–0.09) ceramics for 5G array antenna applications at millimeter-wave frequency

5G polarization converter based on low-temperature co-fired ceramic (LTCC) substrate

High quality of LiMg0.9Zn0.06Ni0.04PO4-TiO2 microwave ceramic and its application for 5G dielectric waveguide bandpass filter

Enhanced Cu2+-substituted Zinc Molybdate Low Temperature Co-Fired Ceramics for Static Microwave Imaging Applications

High Q×f values of Zn-Ni co-modified LiMg0.9Zn0.1-xNixPO4 microwave dielectric ceramics for 5G/6G LTCC modules