Fabrication of liquid-infused porous slippery coating with stability, self-cleaning and corrosion resistance properties for carbon steel

Kaili Zhang,Shouwu Xu,Jun Tan,Xiaojuan Li,Lili Du,Ji Ma,Ping Qiu

DOI: https://doi.org/10.1016/j.colsurfa.2023.131495

2023-04-23

Abstract:Slippery coating has evoked great attention in corrosion protection filed. Improving its lubricating layer stability and mechanical wear resistance is vital to solving the long-term application. In this work, the slippery coating for carbon steel was constructed by spraying silicone oil soaked SiO 2 on the acrylic polyurethane. The SiO 2 particles with irregular coral cluster structures were prepared by a biphasic method. For comparison, the conventional spherical SiO 2 based acrylic polyurethane coating was also prepared. The static contact angle of the slippery coating with coral cluster structured SiO 2 reached 101.3 ° and the sliding angle was 5.4 °, which presented a superior self-cleaning property. After 40 cycles of wear test, the corresponding sliding angle of the coating was 67.6% lower than that of the conventional SiO 2 acrylic polyurethane coating. The charge transfer resistance of the coating derived from EIS tests remained 1.19×10 10 Ω·cm 2 after immersion test for 20 days, which was 3 orders of magnitude higher than that of the conventional SiO 2 coating. In addition, the slippery coating maintains fine sliding performance after being exposed to 0.01 mol/L HCl, 0.01 mol/L NaOH, and 80 °C air respectively. These provided the possibility for its application. The corresponding detailed mechanism was discussed in the paper.

chemistry, physical