Solid-State synthesis of cesium manganese halide nanocrystals in glass with bright and broad red emission for white LEDs

Guangyong Xu,Chuying Wang,Yacong Li,Wen Meng,Guigen Luo,Min Peng,Bin Xu,Zhengtao Deng

DOI: https://doi.org/10.1039/d3sc01084h

IF: 8.4

2023-04-19

Chemical Science

Abstract:Recently, lead halide perovskites nanocrystals (NCs) have attracted extensive attention due to their unique optical properties. However, the toxicity of lead and the instability to moisture obstructs their further commercial development. Herein, a series of lead-free CsMnX 3 (X = Cl, Br, and I) NCs embedded in glasses were synthesized by a high temperature solid-state chemsitry method. These NCs embedded in the glass can remain stable after soaking in water for 90 days. It is found that increasing the amount of cesium carbonate in the synthesis process can not only prevent the oxidation of Mn 2+ to Mn 3+ and promote the transparency of the glass in the 450-700 nm region, but also significantly increase its photoluminescence quantum yield (PL QY) from 2.9% to 65.1%, which is the highest reported value of the red CsMnX 3 NCs so far. Using CsMnBr 3 NCs with red emission peak at 649 nm and full-width-at-half-maximum (FWHM) of 130 nm as the red light source, white light-emitting diodes (LED) devices with International Commission on illumination (CIE) coordinates of (0.33,0.36) and color rendering index (CRI) of 94 were obtained. These findings, together with future research, are likely to yield stable and bright lead-free NCs for the next generation of solid-state lighting.

chemistry, multidisciplinary