Elucidation of C–N bond cleavage mechanism in quinoline hydrodenitrogenation over Pt-based catalysts

Yi-Fan Xue,Jie Feng,Jin-Yao Ma,Wen-Ying Li

DOI: https://doi.org/10.1016/j.ces.2023.119631

IF: 4.7

2023-12-17

Chemical Engineering Science

Abstract:C–N bond breaking is a difficult but crucial step in the quinoline removal of coal-based liquids. Noble metal catalysts have higher C–N bond breaking activity, but their surface bond breaking mechanism is unclear. Atomic layer deposition creates more metal-oxide sites and generates different active species, which facilitates the mechanism study. For this reason, we used atomic layer deposition to deposit TiO 2 on the catalyst surface and suggested a more complete C–N bond breaking mechanism in this study. The particle size and pore structure of the catalyst did not change significantly after the deposition, and the hydrogen adsorption was reduced when there were too many layers deposited and the surface Pt sites were occupied to a high degree. TiO 2 is extremely susceptible to reduction to Ti 3+ under hydrogen, and can change the nature of the electron density of Pt through oxygen vacancies, creating Ti 3+ -Pt δ− sites that are prone to protonation reactions. That means, the occurrence of these protonation reactions not only easily breaks the C–N bond, but also accelerates the rate of C–N bond cleavage due to the increased H coverage on the surface of the xcTi-PtAl catalysts. And the Ti 3+ -Pt δ− sites in catalyst had a stronger adsorption effect on the nitrogen-containing compounds, which in turn lowered the energy barriers of bond cleavage. It is concluded that protonation is a necessary step before the C–N bond can be broken. The subsequent steps were showed by the DFT calculations that the nitrogen-containing compounds adsorbed on the Ti 3+ -Pt δ− sites undergo β-H fracture after the protonation reaction, with the elimination reaction cleaving the C–N bond. The xcTi-PtAl catalysts by atomic layer deposition of Ti not only improve the C–N bond breaking performance, but also improve bond breaking stability by a factor of four compared to the Pt/Al 2 O 3 catalysts.

engineering, chemical