Fluorine-Free and Transparent Superhydrophobic Coating with Enhanced Anti-Icing and Anti-Frosting Performance by Using D26 and KH560 as Coupling Agents

Ting Xiao,Yudian Wang,Xia Lang,Siyu Chen,Lihua Jiang,Fujun Tao,Yequan Xiao,Xinyi Li,Xinyu Tan

DOI: https://doi.org/10.3390/pr12040654

IF: 3.5

2024-03-26

Processes

Abstract:Superhydrophobic surfaces with non-wetting characteristics have been considered to be potential candidates for ice/frost prevention. In this study, a transparent superhydrophobic coating was created by using a simple method that employed (3-glycidoxypropyl) trimethoxysilane (KH560) and 1,2-Bis (trimethoxysilyl) ethane (D26) as coupling agents and epoxy resin (E51) as an adhesive. The synergy between KH560 and D26 significantly improves the long-term outdoor durability, anti-icing, and anti-frosting performance of the superhydrophobic coating. The coating also has good acid and alkali resistance, UV resistance, and durability. The obtained SiO2@E51@KH560@D26 can delay the freezing time of water by 1974 s, much longer than bare glass (345 s) and also longer than the coatings with only D26 (932 s) or with only KH560 (1087 s). Moreover, the SiO2@E51@KH560@D26 showed an improved anti-frosting capability compared with the other three samples and better maintained its superhydrophobic properties at low temperatures. Our study proposes a potential method to fabricate a superhydrophobic coating with both anti-icing and anti-frosting properties.

engineering, chemical

What problem does this paper attempt to address?

The main objective of this paper is to develop a fluorine-free and transparent superhydrophobic coating with enhanced anti-icing and anti-frosting properties. To achieve this goal, the research team employed a simple method to prepare the superhydrophobic coating, using (3-glycidyloxypropyl)trimethoxysilane (KH560) and 1,2-bis(trimethoxysilyl)ethane (D26) as coupling agents and epoxy resin (E51) as an adhesive.

By synergistically utilizing the coupling agents KH560 and D26, the prepared superhydrophobic coating not only significantly improved long-term outdoor durability, anti-icing, and anti-frosting performance but also exhibited good acid and alkali resistance, UV resistance, and durability. Specifically, the resulting SiO2@E51@KH560@D26 coating was able to delay the freezing time of water by 1974 seconds, which is much higher than that of bare glass (345 seconds) and other coatings using only D26 or KH560. Moreover, the coating demonstrated better anti-frosting capability at low temperatures and was able to maintain its superhydrophobic properties well.

Therefore, this study proposes a potential method for manufacturing superhydrophobic coatings with both anti-icing and anti-frosting properties, suitable for large-scale applications, especially in scenarios requiring transparency, such as window surfaces, solar photovoltaic panels, and glass insulators.