Abstract:Linear and star‐shaped poly(ε‐caprolactone‐co‐α‐methylene‐γ‐butyrolactone) P(CL‐co‐MBL) copolyesters with a pendant functional double bond of α‐methylene‐γ‐butyrolactone (MBL) comonomer were used as polymeric precursor for organo‐gels formation. Crosslinking was carried out by light‐initiated thia‐Michael reaction using 1,5‐pentanedithiol (PDT) and pentaerythritol tetrakis(3‐mercaptopropionate) (PETK). Double bond conversion and the content of free thiol groups in the obtained networks was followed and rationally estimated using confocal Raman spectroscopy. The gel content and the crosslinking density varied based on MBL comonomer and crosslinker content and were highest for slight thiol to double bond excess (SH/vinyl; 2/1 molar ratio) while decreasing with further thiol excess. These parameters were more pronounced by the replacement of linear PDT with the star‐shaped PETK crosslinker. The thermal and rheological properties investigation of the obtained materials was performed employing DSC, TGA and using frequency and temperature sweeps rheological measurements. Shear moduli in the range 0.14 up to 0.93 MPa were obtained due to different content of MBL in pre‐polymer and crosslinker in network formation. The strength was caused by the crystalline phase of the PCL segments up to a temperature of 50°C. Formed thioether bond within the network were not reversible up to 150°C as it was found based on temperature sweep rheology. Following, the activation and conversion of thioether bonds within the obtained materials into trialkylsulfonium salts was attained through the alkylation using butyl brosylate. The dynamic nature of the transalkylation at elevated temperature 150°C allowed network rearrangement, which was proved by stress relaxation experiment and investigation of the self‐healing capabilities.

Reversible polymer networks based on polylactide with tetraphenylethane thermally dissociating groups in crosslinks

Structural tuning of polycaprolactone based thermadapt shape memory polymer

Bio-based (co)polylactide-urethane networks with shape memory behavior at body temperature

A New Generation of Poly(lactide/ε-Caprolactone) Polymeric Biomaterials for Application in the Medical Field.

Synthesis and characterization of shape memory poly (ε-caprolactone) networks with programmable and reconfigurable shape-morphing behaviors

Thermoresponsive Star Triblock Copolymers by Combination of Rop and Atrp: from Micelles to Hydrogels

Polyester networks based on Tulipalin A and ε‐caprolactone and activation of the Thioether groups by incorporation of trialkylsulfonium salts

Reprocessability of Dynamic Polydioxaborolane Networks Activated by Heat, Moisture and Mechanical Force

A reversible cross-linked polymer network based on conjugated polypseudorotaxanes

Synthesis, Properties, and Enzymatic Hydrolysis of Poly(lactic acid)-co-Poly(propylene adipate) Block Copolymers Prepared by Reactive Extrusion

Molecular Structure Design and Epoxy Functional Modification of Star-shaped Poly(lactic Acid) by Melt Polycondensation Strategy

Thermally Healable and Reprocessable Polymethacrylate Networks Based on Diol-Mediated Metathesis of 6-Membered Boronic Esters

Solution-based synthesis of a four-arm star-shaped poly(L-lactide)

Selectively Cross-Linked Poly (Lactide)/ethylene-Glycidyl Methacrylate-Vinyl Acetate Thermoplastic Elastomers with Partial Dual-Continuous Network-Like Structures and Shape Memory Performances

Biodegradable Shape‐memory Polymer—polylactide‐co‐poly(glycolide‐co‐caprolactone) Multiblock Copolymer

Ductile Glassy Polymer Networks Capable of Large Plastic Deformation and Elastic Recovery

Synthesis, Structure, and Properties of Polylactide-Based Degradable Shape Memory Polymers

Self‐healing and reprocessing of saturated hydroxyl‐terminated polybutadiene‐based networks enabled by dynamic covalent chemistry

Tuning the Rheological, Thermal, and Solid-State Properties of Branched PLA by Free-Radical-Mediated Reactive Extrusion

Covalent Adaptable Polymethacrylate Networks by Hydrazide Crosslinking Via Isosorbide Levulinate Side Groups

Polylactide-b-poly(ethylene-co-butylene)-b-polylactide thermoplastic elastomers: role of polylactide crystallization and stereocomplexation on microphase separation, mechanical and shape memory properties