Abstract:Rare earth aluminate phosphors are well-known for being nontoxic and environmentally friendly. In this work, Tb3+-doped SrLaAlO4 phosphors were synthesized via a facile high temperature solid-state reaction method. The Optimum reaction temperature is determined to be 1300 degrees C based on the results of powder X-ray diffraction (XRD). The SEM patterns and TEM images correspond with the results of Rietveld refinement and show that the SrLa1-xAlO4:xTb(3+) samples present a flaky structure. The results of photoluminescence spectrums (PL) show that SrLa1-xAlO4:xTb(3+) phosphors can absorb in the UV-vis spectral region of 228 nm-263 nm and exhibit several emission peaks between 450 and 650 run, and the highest peak was at 508 nm. The luminescence properties of SrLa1-xAlO4:xTb(3+) have a strict dependence on the cation substitution levels. When the doping concentration of Tb3+ was 0.05, the emission intensity of the sample is strongest. The thermal quenching result of the SrLa0.95AlO4:xTb(3+) phosphors shows that these phosphors are relatively sensitive to temperature changes under an excitation of 228 nm, as the temperature increases from 25 degrees C to 125 degrees C, the emission intensity (peak at 548 nm) decayed to 55.11% of that at room temperature. However, when the temperature increases to 125 degrees C, the emission intensity (peak at 548 nm) decayed to 61.16% of the initial value under an excitation of 263 nm, which showed a relatively good thermal stability. The internal quantum efficiency (QE) values of the SrLa0.95AlO4:xTb(3+) phosphors was measured and determined to be 48%. Under excitations of 228 nm and 263 nm, the lifetimes of the optimized sample SrLa0.95AlO4:xTb(3+) were 1.3986 ms and 1.2095 ms, respectively, and the CIE coordinates of the sample were calculated as (0.2971, 0.4981), (0.3056, 0.5329), respectively. Under both excitations SrLa0.95AlO4:xTb(3+) exhibited high-color-purity green emission.

Special features of the Faraday effect in rare earth orthoaluminate TbAlO3

Faraday Effect in Tb3+-containing Borate, Fluoride and Fluorophosphate Glasses

Magnetooptics of the Luminescent Transitions in Tb3+:Gd3Ga5O12

Superexchange Interaction Influence on the Faraday Effect in Terbium Fluorophosphate Glasses by Co-doping with Praseodymium, Dysprosium, and Holmium

Faraday Rotation Spectra Analysis Of Bi-Substituted Mixed Rare-Earth Iron Garnet Crystals In Optical Communication Band

Preparation and Faraday effect of fluoroaluminate glasses containing divalent europium ions

Resolving the spin reorientation and crystal-field transitions in Tm FeO 3 with terahertz transient

Luminescence Properties of Magneto-Optical Glasses Containing Tb3+ Ions

Multiferroic Properties in Terbium Orthoferrite

Color-tunable upconversion luminescence of Yb3+, Er3+, and Tm3+ tri-doped ferroelectric BaTiO3 materials

Optical properties and Faraday magneto-optical effects of highly transparent novel Tb2Zr2O7 fluorite ceramics

Energy Transfer among Rare Earth Ions Induced by Annealing Process of Tm-Er Codoped Aluminum Oxide Thin Films

High Field Anomalies of Equilibrium and Ultrafast Magnetism in Rare-Earth-Transition Metal Ferrimagnets

Magneto-optical and fluorescence properties of Tb3+ doped glass-ceramics containing AlPO4

Preparation, Structure, Luminescence Properties of Terbium Doped Perovskite-Like Structure Green-Emitting Phosphors SrLaAlO4:Tb3+

Preparation and cathodoluminescence characteristics of rare earth activated BaAl2O4 phosphors

Optical Study Of Tb-2(Moo4)(3) Crystal

Study on the Faraday Rotation Angle of La-substituted Barium Hexaferrite in the Terahertz Band

Thermoluminescence Spectra of Rare-Earth Doped Calcium Fluoride

Structure, Spin Reorientation and Mössbauer Effect Studies of Tb 0.3 Dy 0.7 (fe 1− X Al X ) 1.95 Alloys

Tb 3 Al 3 Ga 2 O 12 : A Novel Visible–Infrared Faraday Crystal Exhibiting a Superior Magneto-Optical Performance