Abstract:The corrosion behavior of a ferritic unstabilized stainless steel 1.4016 during decomposition of aqueous urea solution at high temperature has been investigated. Corrosion was obtained from 100 h of cyclic heating (from room temperature up to 600 °C) and injection of aqueous urea solution on the steel plate in a laboratory-scale test bench. The evaluation procedure covered the metallographic analysis of corroded steel samples by high-resolution scanning electron microscopy (HR-SEM) and transmission electron microscopy (TEM). Uniform corrosion underneath deposits was found as one of the drivers for degradation of the steel. Damage happened by high-temperature depassivation of stainless steel due to the excess of the aggressive medium. Besides uniform corrosion, a nitridation layer underneath surface oxides together with chromium carbonitride particles precipitated through the whole depth of the sample was identified resulting in intergranular attack.

Corrosion of 1.4016 Ferritic Steel by Urea at High Temperature