Performance of environmentally friendly biopolymer-natural fiber on post-freeze–thaw behavior on silty sand: macro- and micro analysis
Mahmoud Ghazavi,Mobina Taslimi Paein Afrakoti
DOI: https://doi.org/10.1007/s10098-024-03095-4
IF: 4.3
2024-11-30
Clean Technologies and Environmental Policy
Abstract:Silty sandy soils usually have low shear strength due to their non-cohesive structure, weak internal bonds, and high porosity. Environmental challenges, such as freeze–thaw (F–T) cycles, also reduce the mechanical characteristics and instability of infrastructures and structures built on these soils. Biopolymers and fibers offer a sustainable solution to improve soil strength and F–T strength. However, while much research focuses on stabilizing silty sand, fewer studies examine the combined effects of biopolymers and fibers on soil properties under F–T cycles. Additionally, the correlation between ultrasonic pulse velocity (UPV) and unconfined compressive strength (UCS) in biopolymer-stabilized and fiber-reinforced soils still needs to be explored. This study examines the stabilization of silty sand using Persian gum (PG) (0.5–3%) and kenaf fibers (KF) (0–1.5%) with lengths of 6, 12, and 18 mm at the curing times of 7, 28, and 90 days. The samples were subjected to F–T cycles (0, 1, 2, 3, 6, and 12). The results showed that the highest UCS was achieved with 2.5% PG and 1% KF (12 mm) after 28 days. After 12 F–T cycles, the UCS reductions were 41% for sample with 2.5% PG and 34% for sample 2.5% PG and 1%KF. The swelling after freezing for the 2.5% PG and 1% KF sample and the 2.5% PG sample was 4.8% and 3.45%, respectively. A correlation between UPV and UCS after various F–T cycles was suggested. The scanning electron microscopy (SEM) analysis revealed increased voids, weakened polymer bonds, and cracks after 12 F–T cycles.
environmental sciences,green & sustainable science & technology,engineering, environmental