Abstract:In this paper, a chitosan-modified nano-silver solution was used as the core material of an antibacterial agent, and melamine formaldehyde resin was coated onto the core material to obtain the antibacterial microcapsules. The core/wall ratio, the stirring rate, the mass ratio of chitosan to silver ions, and the concentration of the emulsifier were used to carry out four-factor and three-level orthogonal experiments to explore the most significant factors affecting the coverage rate and output of microcapsules and the best preparation technology. The results showed that the concentration of the emulsifier was the most important factor affecting the preparation of microcapsules. The higher the concentration of the emulsifier, the better the dispersed morphology of microcapsules, and the higher the coverage rate, up to 44.0%. The antibacterial coating was prepared by mixing microcapsules with a waterborne primer at a content of 4.0%. Its optical properties, mechanical properties, and antibacterial properties were analyzed. By increasing the concentration of the emulsifier, the gloss of the coating showed a trend of first increasing and then decreasing. When the emulsifier concentration was 2.0%, the gloss of the Andoung wood surface coating reached the maximum value of 21.23%. The influence of emulsifier concentration on the color difference of coating had no obvious law, and it was negatively related to the light transmittance. In terms of mechanical properties, the concentration of the emulsifier is directly proportional to the hardness and impact resistance of the coating, with the maximum reaching 31 kg·cm, and is negatively related to adhesion and roughness. In terms of antibacterial properties, the higher the concentration of the emulsifier, the better the antibacterial properties of the coating. When the concentration of the emulsifier was 4.0%, the antibacterial rates of coating which coated the glass substrate were 71.3% and 80.0% for Escherichia coli and Staphylococcus aureus, respectively. The antibacterial rates of the Andoung wood surface coating reached the maximum, which were 68.4% and 73.2%, respectively, and the antibacterial performance was excellent. In this study, an efficient antibacterial microcapsule for waterborne coatings was prepared, which provided the reference value for the application of antibacterial microcapsules in waterborne coatings.

Preparation of Aloe-Emodin Microcapsules and Its Effect on Antibacterial and Optical Properties of Water-Based Coating

Effect of Different Emulsifiers on the Preparation Process of Aloe-Emodin Microcapsules and Waterborne Coating Properties

Effect of Three Kinds of Aloe Emodin Microcapsules Prepared by SDBS, OP-10 and TWEEN-80 Emulsifiers on Antibacterial, Optical and Mechanical Properties of Water-Based Coating for MDF

Preparation of Chitosan-Modified Nano-Silver Solution Microcapsules and Their Effects on Antibacterial Properties of Waterborne Coatings

Preparation Process Optimization for Melamine Resin-Covered Pomelo Peel Flavonoid Antibacterial Microcapsules and Their Effect on Waterborne Paint Film Performance

Preparation And Application Of Melamine-Urea-Formaldehyde Self-Healing Microcapsules Modified By Nano-Al2o3

Preparation of Antibacterial Nanosilver Solution Microcapsules and Their Impact on the Performance of Andoung Wood Surface Coating

Antimicrobial Edible Coatings and Films from Micro-Emulsions and Their Food Applications.

Comparative Analysis of Performance of Water-Based Coatings Prepared by Two Kinds of Anti-Bacterial Microcapsules and Nano-Silver Solution on the Surface of Andoung Wood

The Effects of Urea–Formaldehyde Resin-Coated Toddalia asiatica (L.) Lam Extract Microcapsules on the Properties of Surface Coatings for Poplar Wood

Effect of Two Types of Pomelo Peel Flavonoid Microcapsules on the Performance of Water-Based Coatings on the Surface of Fiberboard

Preparation of UV Topcoat Microcapsules and Their Effect on the Properties of UV Topcoat Paint Film

Preparation of Microcapsules Coating and the Study of Their Bionic Anti-Fouling Performance

Effect of Microcapsule Concentration with Different Core-Shell Ratios on Waterborne Topcoat Film Properties for Tilia europaea

Enhanced Antifouling Performance with a Synergistic Effect of Self-Renewal Antifouling and Contact Bacteriostasis Via the Ionic Exchange

Effect of Composite Addition of Antibacterial/Photochromic/Self-Repairing Microcapsules on the Performance of Coatings for Medium-Density Fiberboard

Effect of Microcapsules with Waterborne Coating as Core Material on Properties of Coating for Tilia Europaea and Comparison with Other Microcapsules

Effect of Nano-Silver Solution Microcapsules Mixed with Rosin-Modified Shellac Microcapsules on the Performance of Water-Based Coating on Andoung Wood (Monopetalanthus spp.)

Preparation of Shellac Resin Microcapsules Coated with Urea Formaldehyde Resin and Properties of Waterborne Paint Films for Tilia amurensis Rupr.

The Effect of Complex Emulsifier on the Structure of Tung Oil and Phenolic Amides Containing Microcapsules and Its Anti-Fouling and Anti-Corrosion Performances

Preparation of Melamine-Formaldehyde Resin/Rice Husk Powder Coated Epoxy Resin Microcapsules and Effects of Different Microcapsule Contents on the Properties of Waterborne Coatings on Tilia europaea Surface