Abstract:Solid-state lithium (Li) metal batteries are widely used due to their excellent safety, superior energy density, and low cost. Nevertheless, the practical application of solid-state Li batteries is hindered by the inferior ionic conductivity of the solid electrolyte and poor interface contact between the electrode and electrolyte. Herein, a flexible, hybrid ceramic-based electrolyte was fabricated by a solution-casting method using poly(vinylidene fluoride), Li1.4Al0.4Ti1.6(PO4)3 powders, and lithium bis(trifluoromethanesulfonyl)imide. To realize high ionic conductivity and a stable self-viscous electrode/electrolyte interfacial contact simultaneously, a mixed solution of 1-ethyl-3-methylimidazolium bis(trifluoromethanesulfonyl)imide, lithium bis(trifluoromethanesulfonyl)imide, and fluoroethylene carbonate was introduced by the solution-infiltration method. The self-viscous Li1.4Al0.4Ti1.6(PO4)3 ceramic-based electrolyte exhibits superior ionic conductivity (2.4 × 10–4 S cm–1 at 25 °C), a high ionic transference number (0.42), wide voltage window (4.8 V vs Li/Li+), excellent thermal stabilities, and the ability to impede Li dendrite growth. In particular, the stable contact, low interfacial resistance, and fast ion-transport channels between the electrodes and solid electrolytes can be achieved by the self-viscous interfacial layer. The solid-state LiFePO4|Li battery assembled with the solid self-viscous electrolyte demonstrates a satisfactory initial discharge capacity of 138.0 mAh g–1 and capacity retention of 96.5% after 200 cycles at 0.5 C and under 25 °C. The self-viscous modification strategy of the solid electrolyte affords promising options for implementing the intimate electrode/electrolyte interfacial contact in high-energy-density solid-state batteries.The Supporting Information is available free of charge at https://pubs.acs.org/doi/10.1021/acs.energyfuels.1c01202.Figure S1: XRD patterns and SEM image of LATP ceramic powders. Figure S2: Temperature dependence of ionic conductivities for LATP pellets. Figure S3: Flexible and winding performances of self-viscous PLL-LEF electrolyte. Figure S4: Surface morphology of PL and PLL-LEF electrolytes. Figure S5: Adhesiveness exhibitions of PLL-LE composite electrolyte. Figure S6: EIS profiles of 10LiTFSI-40EMITFSI and 10LiTFSI-40EMITFSI-10FEC electrolytes. Figure S7: EIS profiles of stainless steel|PLL-LEF|Li cells. Figure S8: Thermogravimetry curve of PLL-LEF electrolyte. Figure S9: Flammability test of routine Celgard separator. Figure S10: EIS profiles of Li|PLL|Li cell for different aging times. Figure S11: Optical photographs of the PLL electrolyte. Figure S12: Ti 2p XPS of the PLL electrolyte. Figure S13: EIS profiles of Li symmetric cell with different electrolytes after cycling. Figure S14: Constant current cycling curves of Li|PLL-LEF|Li cells at 0.2 mA·cm–2. Figure S15: Constant current cycling curves of Li|PLL-LEF|Li cells at 0.5 mA·cm–2. Figure S16: Constant current cycling curves of Li|PLL-LEF|Li cells. Figure S17: High multiple SEM images of Li surfaces obtained from Li symmetrical cells. Figure S18: SEM image of pristine Li surface. Figure S19: EIS results of LiFePO4|PLL|Li, LiFePO4|PLL-LE|Li and LiFePO4|PLL-LEF|Li batteries. Figure S20: Typical charge–discharge voltage profiles of LiFePO4|PLL-LE|Li cell at 0.5 C. Figure S21: Electrochemical properties of Al2O3@LiNi0.5Co0.3Mn0.3O2|PLL-LEF|Li cell (PDF)This article has not yet been cited by other publications.

Fluorinated Li10GeP2S12 enables stable all‐solid‐state lithium batteries

Homogeneous Fluorine Doping toward Highly Conductive and Stable Li10GeP2S12 Solid Electrolyte for All-Solid-State Lithium Batteries

Enabling superior electrochemical performances of Li10SnP2S12-based all-solid-state batteries using lithium halide electrolytes

Li10Ge(P1–xSbx)2S12 Lithium-Ion Conductors with Enhanced Atmospheric Stability

Integrating Lithium Sulfide as a Single Ionic Conductor Interphase for Stable All-Solid-State Lithium-Sulfur Batteries

Bifunctional Interphase-Enabled Li 10 GeP 2 S 12 Electrolytes for Lithium–Sulfur Battery

A Deformable Dual-Layer Interphase for High-Performance Li10GeP2S12-based Solid-State Li Metal Batteries

Surface Engineered Li Metal Anode for All‐Solid‐State Lithium Metal Batteries with High Capacity

Solid-State Rigid Polymer Composite Electrolytes with In-Situ Formed Nano-Crystalline Lithium Ion Pathways for Lithium-Metal Batteries.

A Stable Polymer‐based Solid‐State Lithium Metal Battery and its Interfacial Characteristics Revealed by Cryogenic Transmission Electron Microscopy

Stable all-solid-state lithium metal batteries enabled by ultrathin LiF/Li3Sb hybrid interface layer

In-situ constructing of dual bifunctional interfacial layers of garnet-type Li6.4La3Zr1.4Ta0.6O12 solid electrolyte towards long-cycle stability for flexible solid metal lithium batteries

Germanium Thin Film Protected Lithium Aluminum Germanium Phosphate for Solid‐State Li Batteries

An All-Solid-State Battery Based on Sulfide and PEO Composite Electrolyte.

Improvement of stability and solid-state battery performances of annealed 70Li2S–30P2S5 electrolytes by additives

PVDF-HFP/LiTFSI based composite solid state electrolyte with different micromorphology of Li6.25Ga0.25La3Zr2O12 doping

Stabilizing Ceramic-Based Electrolyte Interfaces with Self-Viscous Modification Strategy for Solid-State Lithium Batteries

A Polyethylene Oxide Based Electrolyte Enabled by the Synergistic Effect of Active LiGaO2 Filler and Ionic Liquid for Superior Lithium Metal Batteries

Fluorinating All Interfaces Enables Super-Stable Solid-State Lithium Batteries by in Situ Conversion of Detrimental Surface Li2CO3

Toward robust solid-state lithium metal batteries by stabilizing a polyethylene oxide-based solid electrolyte interface with a biomass polymer filler

LiF involved interphase layer enabling thousand cycles of LAGP-based solid-state Li metal batteries with 80% capacity retention