Abstract:The porous carbon derived from Metal Organic Frameworks (MOFs) has aroused great interest because of its considerable specific capacity and the ideal microscopic morphology. However, the structural collapse and agglomeration of MOFs during the synthesis process and annealing process could hamper the specific surface area of the derived carbon, which decreases the electrochemical performance. Therefore, a new strategy that mixing 4,4 '-Dimethyl-2,2 '-bipyridine and 1,3,5-Benzenetricarboxylic acid as mixed-ligands to stabilize the structure of the MOFs is adopted. The adding of 4,4 '-Dimethyl-2,2 '-bipyridine during the synthesis results in the N-Zn-BTC nanotube structure. Furthermore, after annealing and acid treatment, N-doped C nanotube incorporated with pore structure is formed, which shows the specific surface area of 1614.55 m(2) g(-1). The doped nitrogen element introduces the pseudocapacitance during the electrochemical process and improves the wettability of the electrode material simultaneously. And the specific capacitance of N-C electrode can reach 252 F g(-1) at 0.5 A g(-1) and maintain 98.5% of the original specific capacitance after 5000 cycles. Furthermore, a button-type symmetrical supercapacitor based on N-C electrode was assembled, which can reach an energy density of 30 Wh kg(-1) at a power density of 625 W kg(-1) and maintain 86.3% of the capacity after 2000 cycles.

Zeolitic imidazolate frameworks derived carbon with rational porous structure mediated by polyvinylpyrrolidone applied as electrode materials for supercapacitors

Synthesis of Nitrogen-Doped Porous Carbon from Zeolitic Imidazolate Framework-67 and Phenolic Resin for High Performance Supercapacitors

Highly N/O co-doped ultramicroporous carbons derived from nonporous metal-organic framework for high performance supercapacitors

Zeolitic Imidazolate Framework (ZIF-8) Derived Nanoporous Carbon: the Effect of Carbonization Temperature on the Supercapacitor Performance in an Aqueous Electrolyte.

N-Doped Carbon Fibers Derived from Porous Wood Fibers Encapsulated in a Zeolitic Imidazolate Framework as an Electrode Material for Supercapacitors

ZIF-derived mesoporous carbon materials prepared by activation via Na2SiO3 for supercapacitor

In Situ Fabrication of Nitrogen Doped Porous Carbon Nanorods Derived from Metal-Organic Frameworks and Its Application As Supercapacitor Electrodes

Nitrogen-doped macro-meso-micro hierarchical ordered porous carbon derived from ZIF-8 for boosting supercapacitor performance

ZIF-8 Template-Assisted Synthesis of Polyimide-Derived Nitrogen-Oxygen Co-doped Porous Carbon Microspheres for Supercapacitors

Nanoporous Carbons Through Direct Carbonization of a Zeolitic Imidazolate Framework for Supercapacitor Electrodes

Synthesis and Electrochemical Capacitive Properties of Nitrogen-Doped Porous Carbon Micropolyhedra by Direct Carbonization of Zeolitic Imidazolate Framework-11

ZIF-8 Derived Nitrogen-Doped Porous Carbon/carbon Nanotube Composite for High-Performance Supercapacitor

N-doped porous carbon anchoring on carbon nanotubes derived from ZIF-8/polypyrrole nanotubes for superior supercapacitor electrodes

Nitrogen-Doped Nanoporous Carbons Through Direct Carbonization of A Metal-Biomolecule Framework for Supercapacitor

N-Doped hierarchically porous carbon derived from heterogeneous core–shell ZIF-L(Zn)@ZIF-67 for supercapacitor application

Functional Zeolitic-Imidazolate-Framework-Templated Porous Carbon Materials for Co2 Capture and Enhanced Capacitors

Pyrolysis transformation of ZIF-8 wrapped with polytriazine to nitrogen enriched core-shell polyhedrons carbon for supercapacitor

Synthesis of ultrahigh-surface-area nitrogen-doped porous carbon materials from carboxymethyl cellulose based protic polyanion ionic liquids for high performance supercapacitors

ZIF-8-Based Nitrogen and Monoatomic Metal Co-Doped Pyrolytic Porous Carbon for High-Performance Supercapacitor Applications

ZIF-8@MWCNT-derived Carbon Composite As Electrode of High Performance for Supercapacitor

Metal-organic Frameworks-Derived Porous Carbon Nanotube for High Performance Supercapacitor Electrode Materials