Prediction of residual bond strengths between corroded steel bars and concrete after exposure to high temperatures

Tian-Ci Wang,Wan-Yang Gao,Wang-Wei Liu,Jian Liang,Jian Yang

DOI: https://doi.org/10.1016/j.engfracmech.2023.109213

IF: 5.4

2023-03-26

Engineering Fracture Mechanics

Abstract:Reinforced concrete structures used in aggressive environments (e.g., coastal and ocean regions) may suffer from steel corrosion. On the other hand, structures with corroded steel bars are likely to experience fire hazards during their service life. Therefore, the combined effect of high-temperature exposure and steel corrosion may lead to a significant reduction in the post-fire bond strength between the corroded steel bars, and surrounding concrete, which will further affect the residual load-capacity assessment of fire-damaged RC members. This paper presents an analytical model for predicting the residual bond strengths between the corroded steel bars and surrounding concrete after exposure to high temperatures. In the analytical model, the concrete cover around the steel bar is considered as a thick-walled cylinder whose inner surface is subjected to uniform pressure due to the combined action of the pull-out load and the volume expansion of the corrosion products. Three stages of the concrete cover (i.e., uncracked, partially cracked and fully cracked stages) are considered one by one in the analytical model to determine the internal pressure. During the analysis, the tensile softening behavior of the cracked concrete and the material property degradations of concrete after high-temperature exposure are properly considered. The accuracy and reliability of the proposed analytical model are verified by comparing the analytical predictions with the corresponding pull-out test results collected from the literature. A detailed parametric analysis is then performed to gain insight into the effects of various factors on the post-fire residual bond strengths of corroded steel bars.

mechanics