Abstract:In order to efficiently utilize steel slag and reduce carbon emissions, the performance of alkali-activated slag/stainless steel slag mortar (ASM) prepared with a composite activator is investigated. In this work, CaO, Na 2 CO 3 and water glass (WG) are used as composite activators, where the alkali equivalents of CaO and Na 2 CO 3 are maintained at 4% and the alkali equivalents of WG (i.e. WG content) as variables were 0, 0.5%, 1.0%, 1.5% and 2.0% respectively. The properties of ASM, including mechanical properties, autogenous and drying shrinkage, are investigated. Results show that the mechanical properties of ASM decrease and then increase as the WG content increases, with the worst mechanical properties of ASM occurring when the WG content is 0.5%. The autogenous shrinkage of ASM decreases as the WG content increases from 0 to 0.5% followed by an increase as the WG content increases further to 2.0%. Autogenous shrinkage depends on chemical shrinkage, small pore (<50 nm) volume, MCL and capillary pressure. When the WG content is increased from 0 to 0.5%, the hydration reaction is inhibited by the reaction of the WG and CaO which reduces the pH of activator solution and gel amount, leading to a reduction in chemical shrinkage, small pore volume, MCL and capillary pressure. However, the high WG content accelerates the hydration reaction when the WG content is greater than 0.5%, which increases the autogenous shrinkage. The drying shrinkage of ASM decreases and subsequently increases as the WG content increases. The higher drying shrinkage is associated with weight loss due to the excellent connectivity of the pores. The pore structure also affects the drying shrinkage, which can be justified on the basis of capillary pressure.

Effect of polymer latex powder on shrinkage behaviors and microstructure of alkali-activated slag binder

Investigation of shrinkage mechanism of alkali-activated slag

Shrinkage mechanisms and shrinkage-mitigating strategies of alkali-activated slag composites: A critical review

Influence of liquid-binder ratio on the performance of alkali-activated slag mortar with superabsorbent polymer

Influence of Polymer Latexes on the Properties of High Performance Cement–Based Materials

Study on Shrinkage in Alkali-Activated Slag–Fly Ash Cementitious Materials

Effect of Activator and Mineral Admixtures on the Autogenous Shrinkage of Alkali-Activated Slag/Fly Ash

Mitigating the Drying Shrinkage and Autogenous Shrinkage of Alkali-Activated Slag by NaAlO2

Mitigating Autogenous Shrinkage of Alkali-Activated Slag Mortar by Using Porous Fine Aggregates as Internal Curing Agents

Influence of the Activator Concentration and Solid/Liquid Ratio on the Strength and Shrinkage Characteristics of Alkali-Activated Slag Geopolymer Pastes

Effect of CaO on the shrinkage and microstructure of alkali-activated slag/fly ash microsphere

Effects of alkali dosage and silicate modulus on autogenous shrinkage of alkali-activated slag cement paste

Understanding the Role of Metakaolin towards Mitigating the Shrinkage Behavior of Alkali-Activated Slag

Effect of superabsorbent polymer introduction on properties of alkali-activated slag mortar

Effect of borax-modified activator on mechanical properties and drying shrinkage of alkali-activated slag/metakaolin mortar

New Experimental Evidence for Drying Shrinkage of Alkali-Activated Slag with Sodium Hydroxide

Investigation of effects of reactive MgO on autogenous and drying shrinkage of near-neutral salt activated slag cement

Fluidity, mechanical properties, shrinkage of alkali-activated slag/stainless steel slag mortars with composite activators

Effect of Slaked Lime on the Properties of Sodium Sulfate-Activated Alkali-Activated Slag Cement

Effects of Borax, Sucrose, and Citric Acid on the Setting Time and Mechanical Properties of Alkali-Activated Slag

Strength and Drying Shrinkage of Reactive MgO Modified Alkali-Activated Slag Paste