Abstract:316 stainless steel (SS) was coated with CoCrFeNiNbx (x: atomic ratio, x = 0, 0.1, 0.2, and 0.3) high entropy alloy coatings (HEACs) by laser cladding (LC). The impacts of Nb content on the phase composition, microstructure, microhardness, wear resistance and corrosion properties of CoCrFeNi based HEACs were examined. Different from the canonical dendritic (DR) - interdendritic (ID) microstructure presented by the other three HEACs, the ID of Nb0.3 HEACs also existed nanoscale Nb-rich Laves phase composed of Nb-Ni and Nb-Co. The inclusion of Nb significantly reduced the average grain size of CoCrFeNi based HEACs from 59.43 mu m to 11.38 mu m. It also greatly diminished the formation of high angle grain boundaries (HAGBs), increasing the percentage of low angle grain boundaries (LAGBs) from 31 % to 61 %. The microhardness of Nb-containing HEACs was significantly promoted due to the solid solution strengthening and fine grain strengthening caused by large size Nb atoms. Affected by Laves phase with high coordination number and space filling ratio and higher proportion of LAGBs, the microhardness of Nb0.3 HEAC was even as high as 530 HV. The increase in Nb concentration also strengthened the HEACs' resistance to wear. Nb0, Nb0.1, Nb0.2, and Nb0.3 HEACs had corresponding specific wear rates of 0.36, 0.32, 0.23, and 0.20 mm3/Nm. Unlike 316 SS, Nb0 and Nb0.1 HEACs, which had both adhesive wear and abrasive wear, Nb0.2 and Nb0.3 HEACs were mainly wear by abrasive wear. The corrosion behavior of CoCrFeNiNbx HEACs in 0.5 M H2SO4 solution was similar to 316 SS, but the corrosion resistance was stronger than 316 SS. Nb0.3 HEAC with the Ecorr of -164 mV and Icorr of 6.40 x 10-7 A/cm2 showed the best acid corrosion resistance, which could be attributed to the stable and dense passivation film on its surface. Distinct from the intergranular corrosion of other coatings, the corrosion of Nb0.3 HEAC mainly occurred in DR, because the FCC phase acted as the anode site in it when FCC and Laves phase co-existed.

Electrochemical Behavior and Surface Chemistry Studies of Electrodeposited MnMoCrCoFeNiCu High Entropy Alloy-Carbon Nanotube Composite Coatings

Evolution of Surface Oxide Chemistry and its Effect on the Electrochemical Degradation Behaviour of AlCoFeCuNi High Entropy Alloy Coating Incorporated with Multiwalled Carbon Nanotubes

Phase composition, surface chemistry and electrochemical studies of electrodeposited AlMnFeCuNi high entropy alloy composite coatings incorporated with carbon nanotubes

Electrochemical Corrosion Behavior in Sulfuric Acid Solution and Dry Sliding Friction and Wear Properties of Laser-Cladded CoCrFeNiNb High Entropy Alloy Coatings

Microstructure and Corrosion Properties of Crmnfeconi High Entropy Alloy Coating

Microstructures, Physical and Corrosion Behavior of NiCoFeCu High-Entropy Alloy Nanocomposite Coatings Electro-Co-deposited with Nano-Si3n4 Particles

Microstructure and Corrosion Properties of Electrodeposited CoCrFeMnNi High Entropy Alloy Coatings

Microstructural Features, Corrosion and Wear Behavior of the AlCrFeCoNiCu High-Entropy Alloy, Electrodeposited Coatings, and Subsequent Heat Treatment

Structure and corrosion behavior of FeCoCrNiMo high-entropy alloy coatings prepared by mechanical alloying and plasma spraying

Tailoring Microstructure and Corrosion Behavior of CoNiCrFeMoBSi High-Entropy Alloy Coatings Via Mo Addition

Structural and electrochemical corrosion properties of plasma-sprayed CoCrFeNiMo HEA coating in corrosive solutions

CoCrFeMnNi0.8V/Cr3C2-Ni20Cr High-Entropy Alloy Composite Thermal Spray Coating: Comparison with Monolithic CoCrFeMnNi0.8V and Cr3C2-Ni20Cr Coatings

Microstructural and Tribological Behavior of Thermal Spray CrMnFeCoNi High Entropy Alloy Coatings

Microstructure and Properties of FeCrMnxAlCu High-Entropy Alloys and Coatings

Influence of Heat Treatment on Microstructural, Corrosion and Tribological Behaviour of Electrodeposited AlCoFeMnNiCu High Entropy Alloy Coatings

Electrodeposited FeCoNiWMo high entropy alloy/SiC nanocomposite coatings: Microstructure, mechanical properties and corrosion resistance

Microstructures and Corrosion Behaviors of Non-Equiatomic Al0.32CrFeTi0.73(Ni1.50−xMox)(x = 0, 0.23) High-Entropy Alloy Coatings Prepared by the High-Velocity Oxygen Fuel Method

Corrosion resistance and wear behavior of CoCrFeNiMn@Gr high entropy alloy-based composite coatings prepared by laser cladding

Tribological and electrochemical behaviors of FeCoNiCrMox HEA coatings prepared by internal laser cladding on 316L steel tube

Electrochemical Deposition and Corrosion Resistance Characterization of FeCoNiCr High-Entropy Alloy Coatings

Mechanically Alloyed CoCrFeNiMo0.85 High-Entropy Alloy for Corrosion Resistance Coatings