The Effect of Different Diluents and Curing Agents on the Performance of Epoxy Resin-Based Intumescent Flame-Retardant Coatings

Xukun Yang,Yange Wan,Nan Yang,Yilin Hou,Dantong Chen,Jiachen Liu,Guoshuai Cai,Mingchao Wang

DOI: https://doi.org/10.3390/ma17020348

IF: 3.4

2024-01-11

Materials

Abstract:The epoxy resin-based (ESB) intumescent flame-retardant coatings were modified with 1,4-butanediol diglycidyl ether (14BDDE) and butyl glycidyl ether (BGE) as diluents and T403 and 4,4′-diaminodiphenylmethane (DDM) as curing agents, respectively. The effects of different diluents and curing agents on the flame-retardant and mechanical properties, as well as the composition evolution of the coatings, were investigated by using large-plate combustion, the limiting oxygen index (LOI), vertical combustion, a cone calorimeter, X-ray diffraction, FTIR analysis, a N2 adsorption and desorption test, a scanning electron microscope (SEM), a tensile strength test, and a viscosity test. The results showed that the addition of 14BBDE and T403 promoted the oxidation of B4C and the formation of boron-containing glass or ceramics, increased the residual mass of char, densified the surface char layer, and increased the specific surface area of porous residual char. When their dosage was 30%, ESB-1T-3 coating exhibited the most excellent flame-retardant properties. During the 2 h large-plate combustion test, the backside temperature was only 138.72 °C, without any melting pits. In addition, the peak heat release rate (PHRR), total heat release rate (THR), total smoke production (TSP), and peak smoke production (PSPR) were reduced by 13.15%, 13.9%, 5.48%, and 17.45%, respectively, compared to the blank ESB coating. The LOI value reached 33.4%, and the vertical combustion grade was V-0. In addition, the tensile strength of the ESB-1T-3 sample was increased by 10.94% compared to ESB. In contrast, the addition of BGE and DDM promoted the combustion of the coating, affected the ceramic process of the coating, seriously affected the formation of borosilicate glass, and exhibited poor flame retardancy. The backside temperature reached 190.93 °C after 2 h combustion. A unified rule is that as the amount of diluent and curing agent increases, the flame retardancy improves while the mechanical properties decrease. This work provides data support for the preparation and process optimization of resin-based coatings.

materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,metallurgy & metallurgical engineering

What problem does this paper attempt to address?

The paper attempts to address the issue of studying the effects of different diluents and curing agents on the performance of epoxy resin-based intumescent fire-retardant coatings (ESB). Specifically, the paper explores the impact of 1,4-Butanediol diglycidyl ether (14BDDE) and Butyl glycidyl ether (BGE) as diluents, and T403 and 4,4′-Diaminodiphenylmethane (DDM) as curing agents, on the fire-retardant performance, mechanical properties, and coating composition evolution of the coatings.

The main objectives of the study include:
1. **Enhancing fire-retardant performance**: Improving the fire-retardant effect of the coatings at high temperatures by adding different types of diluents and curing agents, reducing heat release and smoke generation during combustion.
2. **Optimizing mechanical properties**: Ensuring that the mechanical strength of the coatings, such as tensile strength, is not significantly reduced while enhancing fire-retardant performance.
3. **Adjusting the coating preparation process**: Reducing the viscosity of the coatings by selecting appropriate diluents and curing agents, making them easier to apply in practical engineering while maintaining their fire-retardant and mechanical properties.

The paper systematically evaluates the effects of different diluents and curing agents on the performance of the coatings through a series of experiments, including large-scale panel combustion tests, Limiting Oxygen Index (LOI) tests, vertical combustion tests, and cone calorimeter tests, and draws specific conclusions. These conclusions provide important data support for the preparation and process optimization of epoxy resin-based fire-retardant coatings.