Influence of compressive load and heat treatment on deformation luminescence of KCl:Eu2+ single crystals exposed to X-ray
Yohichi KohzukiDepartment of Mechanical Engineering,Saitama Institute of Technology,Saitama,JapanYohichi Kohzuki is currently a professor at Department of Mechanical Engineering,Saitama Institute of Technology,Saitama,Japan. He received a Master of Engineering from Osaka Industrial University in 1991 and received a Doctor of Engineering from Kanazawa University in 1994. He began his career at Kewpie Corporation,as a factory staff in 1988. He was a research student at Faculty of Engineering,Kanazawa University,in 1995 and worked as a part time lecturer at Kanazawa University Liberal Arts and Science,Kanazawa,in 1995–2004; a part time lecturer at Ishikawa Prefectural Vocational Training Centre Kanazawa,Kanazawa,in 2001–04; an assistant teacher at Ishikawa Prefectural Kanazawa Izumigaoka Senior High School,Kanazawa,in 2003; a calibrator at Navy Calibration Laboratory Iwakuni,Iwakuni,in 2005–06; an associate professor in 2006–14 and a professor in 2014–15 at National Institute of Technology,Oshima College,Yamaguchi; a professor at Department of Mechanical Engineering,Saitama Institute of Technology,Saitama,in 2015–. He has studied in the field of crystal plasticity,mechanical properties,and deformation luminescence. In the microscopic viewpoint based on dislocation motion during plastic deformation,he has authored approximately 90 articles (international journals,chapters,etc.) so far.
DOI: https://doi.org/10.1080/10420150.2023.2294467
2024-01-16
Radiation Effects and Defects in Solids
Abstract:When KCl:Eu 2+ single crystals were exposed to X-ray and were plastically deformed by compression at 50 μm min −1 , the peak appears around 330 K on the thermoluminescence (TL) glow curve under the influence of the compressive load below 200 N. The peak is termed 330 K peak here. Its intensity becomes slightly large with the compressive load and also depends on the quenching temperature above about 473 K for the preparation of sample. Furthermore, the 330 K peak disappears on the TL glow curve by the heat treatment: annealing at 953 K for 16 h, followed by gradually cooling to room temperature within 24 h. The variations in the 330 K peak height are related to the density of dislocations in the sample. On the absorption spectrum for the crystal, the peak height at the wavelength of 560 nm decreases by the heat treatment. This result is supposed to be caused by the phenomenon that dislocation density is reduced and some colour centres on the 330 K peak etc. are removed in the annealing process of the crystal.
physics, condensed matter, fluids & plasmas,nuclear science & technology