Rejuvenation behavior and microstructural evolution of Cu-Zr metallic glass during multiple recovery annealing treatment via molecular dynamic simulation

Mingzi Wang,Shulin Lü,Shusen Wu,Wei Guo

DOI: https://doi.org/10.1016/j.jallcom.2023.169294

IF: 6.2

2023-02-18

Journal of Alloys and Compounds

Abstract:The evolution of structural characteristics and mechanical properties of Cu-Zr metallic glasses during multiple recovery annealing process was investigated via molecular dynamics simulation. Firstly, the aged and rejuvenated samples were prepared after the first recovery annealing by varying the annealing temperature. Then, these samples were subsequently treated with the following annealing process. It is found that when reheating the firstly aged sample (annealing at 900 K) to a higher annealing temperatures of 1100 K at the second annealing, the degree of rejuvenation was even higher than that of the initially rejuvenated sample (annealing at 1100 K) at the same temperature. Microstructural analysis shows that the degree of rejuvenation shows a strong correlation with Cu-centered clusters, around a 4% difference in (high local fivefold symmetry) content between the most aged and most rejuvenated samples. Moreover, the volume variation of different atomic clusters in the rejuvenated samples is more obvious. It is noted that the initial aged samples can be rejuvenated to an even higher degree when compared with initial rejuvenated ones. The more icosahedral clusters in the aged sample contributes to such phenomenon since they are more easily modified to other types with low local fivefold symmetry at high annealing temperature during the second annealing. The present study demonstrates that the appropriate multiple recovery annealing can rejuvenate the sample to a higher degree.

materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering