Abstract:The growing interest in the use of building materials with a reduced carbon footprint was the aim of this research assessing the impact of four different types of low-emission cements on the properties of cement concretes used for the construction of local roads. This research work attempted to verify the strength characteristics and assess the durability of such solutions, which used the commonly used CEM I 42.5 R pure clinker cement and three multi-component cements: CEM II/A-V 42.5 R, CEM III/A 42.5 N-LH/HSR/NA, and CEM V/A S-V 42.5 N-LH/HSR/NA. Cement was used in a constant amount of 360 kg/m3, sand of 0/2 mm, and granite aggregate fractions of 2/8 and 8/16 mm. This research was carried out in two areas: the first concerned strength tests and the second focused on the area of assessing the durability of concrete in terms of frost resistance F150, resistance to de-icing agents, water penetration under pressure, and an analysis of the air entrainment structure in concrete according to the PN EN 480-11 standard. Analyzing the obtained test results, it can be concluded that the highest compressive strength of more than 70 MPa was obtained for CEM III concrete, 68 MPa for CEM V concrete, and the lowest for CEM I cement after 90 days. After the durability tests, it was found that the smallest decrease in compressive strength after 150 freezing and thawing cycles was obtained for CEM III (−0.9%) and CEM V (−1.4%) concretes. The high durability of concrete is confirmed by water penetration tests under pressure, because for newly designed recipes using CEM II, CEM III, and CEM V, water penetration from 17 mm to 18 mm was achieved, which proves the very high tightness of the concrete. The assessment of the durability of low-emission cements was confirmed by tests of resistance to de-icing agents and the aeration structure performed under a microscope in accordance with the requirements of the PN-EN 480-11 standard. The obtained analysis results indicate the correct structure and minimal spacing of air bubbles in the concrete, which confirms and guarantees the durability of concrete intended for road construction. Concretes designed using CEM V cement are characterized by a carbon footprint reduction of 36%, and for the mixture based on CEM III, we even observed a decrease of 39% compared to traditional concrete. Concrete using CEM II, CEM III, and CEM V cements can be successfully used for the construction of local roads. Therefore, it is necessary to consider changing the requirements of the technical specifications recommended for roads in Poland.

Life cycle assessment of lightweight cellular concrete subbase pavements in Canada

In-situ structural analysis of lightweight cellular concrete subbase flexible pavements

Structural capacity evaluation of lightweight cellular concrete for flexible pavement subbase

Effects of Mix Design and Functional Unit on Life Cycle Assessment of Recycled Aggregate Concrete: Evidence from Co2 Concrete

Ensemble and evolutionary prediction of layers temperature in conventional and lightweight cellular concrete subbase pavements

Carbon Accounting for Permeable Pavement Based on the Full Life Cycle Approach and Its Application

Overview of Pavement Life Cycle Assessment Use Phase Research at the MIT Concrete Sustainability Hub

Comparative Life Cycle Assessment of Asphalt Mixtures Using Composite Admixtures of Lignin and Glass Fibers

A comparative life cycle assessment (LCA), life cycle cost analysis (LCCA), mechanical and long-term leaching evaluation of road pavement structures containing multiple secondary materials

Comparative life cycle assessment of a novel sustainable road pavement system adopting recycled plastic from PET bottles and carbonated aggregate

Life cycle assessment (LCA) of precast concrete blocks utilizing ground granulated blast furnace slag

Life Cycle Assessment (LCA) of Alternative Pavement Rehabilitation Solutions: A Case Study

Life Cycle Assessment of Greenhouse Gas Emissions from Recycled Asphalt Pavement Production

Life cycle assessment of sustainable concrete with recycled aggregate and supplementary cementitious materials

Life Cycle Assessment in Road Pavement Infrastructures: A Review

Evaluation of the optimum value of lightweight expanded clay aggregate incorporation into the roller-compacted concrete pavement through experimental measurement of mechanical and thermal properties

Analysis on determinants of carbon emissions from plaza ground paving during the construction stage based on life cycle assessment

Comparative life cycle assessment of natural and recycled aggregate concrete: A review

Performance Research of Cement Concrete Pavements with a Lower Carbon Footprint

Assessing life cycle sustainability: A comprehensive review of concrete produced from construction waste fine fractions

Characteristics of Lightweight Concrete Fabricated with Different Types of Strengthened Lightweight Aggregates