A highly durable zinc-air battery from directly integrated FexNC@NiFe(OH)x bifunctional catalyst

Hao Luo,Yang Li,Wenchao Wang,Tao Zhou,Zhengxiao Guo

DOI: https://doi.org/10.1039/d2qi02564g

IF: 7.779

2023-02-03

Inorganic Chemistry Frontiers

Abstract:Rechargeable Zinc-air Batteries (ZABs) hold great promise for energy storage and conversion due to their high theoretical energy density, cost-effectiveness and inherent safety. However, progresses are constrained by the sluggish oxygen electrocatalysis and instability at the air cathode. To address such issues, we resorted to a directly integrated pseudo-3D composite electrocatalyst based on carbon cloth, on which Fe/Fe3C- and N- co-doped carbon nanotubes are directly induced, and then used to further intercalate NiFe hydroxide clusters, FexNC@NiFe(OH)x . This hierarchical electrocatalyst shows enhanced oxygen electrocatalysis (ΔE is 626 mV), rendering high efficiency and durability of ZABs. Such improvement can be attributed to the rationally integrated pseudo-3D structure of high conductivity, high density of active sites, interconnected porosity and well-bonded components for accelerating electron transfer and ion diffusion while ensuring structural integrity. Moreover, the hierarchical structure increases the electrochemical surface area with superior surface hydrophilicity. As a result, the composite electrocatalyst shows great potential as a binder-free air electrode, as demonstrated in a rechargeable Zn-air battery of a high power density of 85.1 mW cm-2 and a long period of operation beyond 2000 cycles (350 hours) without notable degradation, outperforming noble metal electrodes.