Properties of Carbon Fibers as Supercapacitor Electrodes via Electrospinning Using a Blending Solution of Polyacrylonitrile and Bisphenol A

Ji-Woo Park,Young-Wan Ju

DOI: https://doi.org/10.3390/en17071732

IF: 3.2

2024-04-04

Energies

Abstract:Supercapacitors have attracted attention as efficient energy storage systems owing to their high power density and cycling stability. The use of appropriate electrode materials is important for high-performance supercapacitors, and various carbon materials have been studied as supercapacitor electrodes. In this study, carbon nanofibers with high specific surface areas were fabricated via a simple electrospinning process. Carbon nanofibers were fabricated by adjusting the ratio of polyacrylonitrile (PAN) to bisphenol A (BPA) and evaluated as electrode materials for supercapacitors. With the addition of BPA, improved specific surface area and oxygen functional groups were observed compared with nanofibers using only PAN. Therefore, BPA3, which had the highest specific surface area, exhibited a 28% improvement in capacitance (162 F/g) compared with BPA0 fabricated using only PAN. Carbon nanofibers fabricated by adjusting the ratio of BPA to PAN are promising electrodes for supercapacitors owing to their high capacitance and stability.

energy & fuels

What problem does this paper attempt to address?

The main purpose of this paper is to investigate the characteristics of carbon fibers prepared by electrospinning polyacrylonitrile (PAN) and bisphenol A (BPA) mixed solution as electrodes for supercapacitors. In this study, the authors adjusted the ratio of PAN to BPA to optimize the specific surface area and oxygen functional groups of carbon nanofibers, thereby improving the capacitive performance of supercapacitors.

The main objective of the paper is to improve the capacitive performance of carbon fiber electrodes, especially those prepared by electrospinning carbon nanofibers. It was found that by adding BPA, the specific surface area and oxygen functional groups of carbon fibers can be increased, thereby enhancing the capacitance (up to 162 F/g), which is 28% higher than that of the BPA0 system using only PAN. Meanwhile, by adjusting the BPA ratio, electrode materials with high capacitance and stability can be obtained, which are suitable for supercapacitors.

Experimental results show that BPA-containing carbon nanofibers have better micropore and mesopore development, while BPA5 forms bead-like structures due to its low viscosity. Therefore, BPA3 is considered the optimal BPA ratio, exhibiting excellent electrochemical performance and stability. Even after 2000 cycles, the capacity decay rate is only 3.2%. These findings suggest that by adjusting the ratio of PAN to BPA, carbon nanofiber electrodes can be effectively improved to enhance the energy storage capacity of supercapacitors.