Functional surface modification of P2-type layered Mn-based oxide cathode by thin layer of NASICON for sodium-ion batteries

Yuqiu Shao,Xinxin Wang,Bingchen Li,Huirong Ma,Jingjing Chen,Dajian Wang,Chenlong Dong,Zhiyong Mao

DOI: https://doi.org/10.1016/j.electacta.2023.141915

IF: 6.6

2023-01-21

Electrochimica Acta

Abstract:P2-type layered manganese-based oxides, as promising high-energy-density and low-cost cathodes, have been triggered considerable attentions in sodium ion batteries (SIBs). Nevertheless, P2-type manganese-based oxides still suffer from the sluggish kinetics and unfavorable Jahn-Teller effect. Herein, motivated by the high ionic conductivity and rigid three-dimension framework of NASICON-type materials, the well-known Na 3 Zr 2 Si 2 PO 12 thin layer was coated on P2-type Na 0.612 K 0.056 MnO 2 surface to modify electrochemical sodium storage and structural stability. The optimal Na 0.612 K 0.056 MnO 2 @Na 3 Zr 2 Si 2 PO 12 exhibited a high discharge capacity of 203 mA h g − 1 within 1.8 − 4.3 V at a low current density of 10 mA g − 1 . When the current density enhances into 500 mA g − 1 , it delivers a high initial discharge capacity of 145.7 mA h g −1 within 1.8 − 4.3 V at 500 mA g −1 and maintains 69% capacity retention after 100 cycles. Besides, at low temperature of −20 °C, it offers 100.1 mA h g − 1 after 100 cycles within 1.8 − 4.3 V at 100 mA g − 1 , which is much higher than that of NKMO (65.2 mA h g − 1 ). The Na 3 Zr 2 Si 2 PO 12 can decrease Mn 3+ content and avoid the Jahn-Teller effect of Na 0.612 K 0.056 MnO 2 in structural level, enabling the enhanced Na + diffusion coefficient of Na 0.612 K 0.056 MnO 2 . Such strategy NASICON coating on cathode would pave a new pathway on rational design of high-performance cathode for SIBs.

electrochemistry