Abstract:Binary Mg–Ca alloys with various Ca contents were fabricated under different working conditions. X-ray diffraction (XRD) analysis and optical microscopy observations showed that Mg–xCa (x=1–3 wt%) alloys were composed of two phases, α(Mg) and Mg2Ca. The results of tensile tests and in vitro corrosion tests indicated that the mechanical properties could be adjusted by controlling the Ca content and processing treatment. The yield strength (YS), ultimate tensile strength (UTS) and elongation decreased with increasing Ca content. The UTS and elongation of as-cast Mg–1Ca alloy (71.38±3.01MPa and 1.87±0.14%) were largely improved after hot rolling (166.7±3.01MPa and 3±0.78%) and hot extrusion (239.63±7.21MPa and 10.63±0.64%). The in vitro corrosion test in simulated body fluid (SBF) indicated that the microstructure and working history of Mg–xCa alloys strongly affected their corrosion behaviors. An increasing content of Mg2Ca phase led to a higher corrosion rate whereas hot rolling and hot extrusion could reduce it. The cytotoxicity evaluation using L-929 cells revealed that Mg–1Ca alloy did not induce toxicity to cells, and the viability of cells for Mg–1Ca alloy extraction medium was better than that of control. Moreover, Mg–1Ca alloy pins, with commercial pure Ti pins as control, were implanted into the left and right rabbit femoral shafts, respectively, and observed for 1, 2 and 3 months. High activity of osteoblast and osteocytes were observed around the Mg–1Ca alloy pins as shown by hematoxylin and eosin stained tissue sections. Radiographic examination revealed that the Mg–1Ca alloy pins gradually degraded in vivo within 90 days and the newly formed bone was clearly seen at month 3. Both the in vitro and in vivo corrosion suggested that a mixture of Mg(OH)2 and hydroxyapatite formed on the surface of Mg–1Ca alloy with the extension of immersion/implantation time. In addition, no significant difference (p>0.05) of serum magnesium was detected at different degradation stages. All these results revealed that Mg–1Ca alloy had the acceptable biocompatibility as a new kind of biodegradable implant material. Based on the above results, a solid alloy/liquid solution interface model was also proposed to interpret the biocorrosion process and the associated hydroxyapatite mineralization.

Comparative Study on the Microstructure and Biodegradation Behavior of Commercialized Pure Mg and Mg-1.0Ca-0.5Sr Alloy in 27 mM HCO3−-SBF: The Influence of the pH Regulation Treatments

Effect of pH on the degradation kinetics of a Mg–0.8Ca alloy for orthopedic implants

Corrosion Degradation of AXJ530 Magnesium Alloy in Simulated Pysiological Fluid and Its Mitigation by Fluoride and Chitosan Coatings for Osteosynthetic Applications

<i>In vitro</i> degradation behavior of as-cast Mg-3Zn-1Ca-0.5 Sr alloy

Electrochemical techniques for monitoring the biodegradability of nanocomposite Mg-alloy/HA for repairing bone fracture

In Vivo and in Simulated Body Fluid Degradation Behavior and Biocompatibility Evaluation of Anodic Oxidation-Silane-chitosan-coated Mg-4.0Zn-0.8Sr Alloy for Bone Application.

High-purity Mg and Mg-1Ca alloys: Comparative assessment of the merits regarding degradation, osteogenesis, and biosafety for orthopedic applications

Corrosion Resistance and Cytocompatibility of Biodegradable Surgical Magnesium Alloy Coated with Hydrogenated Amorphous Silicon.

Effect of Strontium-Substituted Calcium Phosphate Coatings Prepared by One-Step Electrodeposition at Different Temperatures on Corrosion Resistance and Biocompatibility of AZ31 Magnesium Alloys

The Development of Binary Mg-Ca Alloys for Use As Biodegradable Materials Within Bone

Comparison Study of Different Coatings on Degradation Performance and Cell Response of Mg-Sr Alloy

In Vitro Corrosion and Cytocompatibility of A Microarc Oxidation Coating and Poly(L-Lactic Acid) Composite Coating on Mg-1li-1ca Alloy for Orthopedic Implants

Degradation and biocompatibility of a series of strontium substituted hydroxyapatite coatings on magnesium alloys

In Vitro Degradation and Mechanical Integrity of Mg-Zn-Ca Alloy Coated with Ca-deficient Hydroxyapatite by the Pulse Electrodeposition Process.

Effect of the Second-Step Voltages on the Structural and Corrosion Properties of Silicon–calcium–phosphate (si–cap) Coatings on Mg–Zn–Ca Alloy

In vivo comparison of the degradation and osteointegration properties of micro-arc oxidation-coated Mg-Sr and Mg-Ca alloy scaffolds

Effects of Hydrogen Peroxide and Ph on Corrosion Behavior of a Biodegradable As-Extruded Mg-0 .5 Sr Alloy

In Vitro Degradation and Electrochemical Corrosion Evaluations of Microarc Oxidized Pure Mg, Mg-Ca and Mg-Ca-Zn Alloys for Biomedical Applications

Effect of Sr on the Microstructure and Biodegradable Behavior of Mg–Zn–Ca-Mn Alloys for Implant Application

Tailoring Biodegradation of Mg-Ca Alloy by Acid Pickling and Polydioxanone/n-Hydroxyapatite Composite Coating for Temporary Implant Applications

Evaluation on the corrosion resistance, antibacterial property and osteogenic activity of biodegradable Mg-Ca and Mg-Ca-Zn-Ag alloys