Tailoring Strategies to Enhance the Photoelectrocatalytic Activity of Perovskite Oxide Surfaces ABO3 for Efficient Renewable Energy Generation
J. Manuel Mora-Hernandez,Leticia M. Torres-Martínez
DOI: https://doi.org/10.1007/978-3-030-74073-3_6
2021-01-01
Abstract:The chapter covers topics focused on analyzing and discussing structural, morphological, optical, and electrochemical parameters presented by advanced inorganic perovskites with general formula ABO3 to carry out the photocatalytic hydrogen generation efficiently. The chapter deals with the synthesis, controlled modification, and photocatalytic evaluation for LaBO3 (M = Co, Mn, Fe) and ATiO3 (A = Zn, Cd, Pb) metal transition perovskite families; as well as the modification of LaBO3 perovskites through the formation of g-C3N4/LaBO3 heterostructures. It also analyzes the photoelectrocatalytic activity of an efficient BaBiO3/NaTaO3 heterojunction that improves the charge transfer mechanisms and decreases the charge carrier’s recombination. The substitution of cation A in ATiO3 (A = Zn, Cd, Pb) promoted important structural changes. CdTiO3 and ZnTiO3 crystallized in a rhombohedral structure; additionally, traces of TiO2 caused by instability at high temperatures were found in ZnTiO3. Since Pb2+ cation has the appropriate size to occupy the A position in the perovskite structure (1.19 Å), PbTiO3 presents a more symmetrical structure with a closer angle to 180°. On the other hand, Cd and Zn cations with lower ionic radius present structural empty sites, creating a higher number of structural distortions. In the LaBO3 (B: Co, Fe, Mn) family, the cation with the highest ionic radius (Co3+, 2.18 Å) presents the closest angle to 180°, which results in a highly ordered structure. Because the optical properties are closely related to the B cation’s energy levels, the Ti-3d levels are involved in the conduction band. However, the energy levels of Pb3+ are lower than the 3d levels of titanium, so it was possible to observe an optical redshift. On the other hand, LaBO3 materials (B = Co, Mn, Fe) show drastic changes once the B cation is replaced; particularly, Mn and Co cations present absorption in the entire range of the visible spectrum, which is attributed to the presence of lower energy (d→d) transitions. Regarding the H2 production, LaMnO3 and ZnTiO3 show the highest hydrogen production (103μmol g−1 and 130μmol g−1, respectively); such enhanced activity is related to the presence of La2O3 and TiO2 as additional phases. The formation of a ZnTiO3/TiO2 heterostructure improves the charge separation. For LaMnO3, the lanthanide 4f level plays an important role in the interfacial charge transfer; a more symmetrical and defect-free structure improves the load transport onto the material surface. Despite the efficient initial photocatalytic activity, LaBO3 (B: Co, Fe, Mn) materials showed a deactivation process; such feature was attributed to a surface blockage by oxygenated species, particularly CO3-2 and OH−. Since the heterojunction formation improved LaMnO3 and ZnTiO3 performance, two new efficient heterostructures, BaBiO3/NaTaO3 and g-C3N4/LaBO3 (B: Co, Fe, Mn), were synthesized. It was determined the g-C3N4/2%LaFeO3 (type-ll heterostructure) showed the best photocatalytic performance (140μmol g−1). Above 2 wt.% of LaFeO3, the g-C3N4 active sites are blocked, resulting in reduced light absorption, and increased recombination rate. On the other hand, the addition of 20 wt.% BaBiO3 to NaTaO3 improves the absorption of light in the visible range and increases the heterostructure crystallite size, thus promoting a lower number of grain boundary defects, reducing the charge carrier’s recombination rate. Therefore, this chapter aims to present strategies that improve photocatalytic activity by modifying the internal, morphological, and surface structure of active perovskite materials.