Abstract:Finding new methods to design environmentally friendly, highly stable, and robust oxygen evolution reaction (OER) and hydrogen evolution reaction (HER) catalysts remains an extremely important challenge and affords several opportunities for exploiting the water-splitting process. In our work, Cu-Co-M (M = O, S, P, Se, S-P, and P-S) materials were grown in situ on three-dimensional (3D) porous nickel foam (NF) with good electrical conductivity by hydrothermal synthesis, vulcanization, selenylation, and phosphorization of the Cu-Co-precursor under an Ar atmosphere. Cu-Co-P-S/NF presents an overpotential value of 220 mV at 50 mA cm-2 for OER and that for Cu-Co-P-S/NF of 120 mV at 10 mA cm-2 for HER in an alkaline medium. In addition, considering the superior activities of Cu-Co-P-S/NF for OER and HER, the electrode pairing of Cu-Co-P-SOER//Cu-Co-P-SHER is designed for overall water splitting, and the experimental result shows that only a cell voltage of 1.55 V is needed to obtain a current density of 20 mA cm-2. According to the literature, this cell voltage is also among the lowest values that have been previously reported for electrocatalytic water splitting. Further, Cu-Co-P-S//Cu-Co-P-S exhibited efficient stability during a 20 h durability test without significant attenuation under alkaline conditions. By using XPS spectroscopy characterization, it was shown that Cu-Co-P-S presented the highest catalytic performance and long-term durability owing to the abundance of Co3+. The novelty of selecting the highest activity with the same catalyst for OER and HER from Cu-Co-M (M = O, S, P, Se, S-P, and P-S) in order to obtain a well-matched electrode pair, and therefore, simplifying the water-splitting device affords a wide range of possibilities for further exploitation of environmentally friendly and highly efficient electrode pairs.

Synthesis of bristlegrass-like Co-doped Ni 2 P composites on Ni foam for overall seawater splitting

N, P co-doped Ni/Mo-based multicomponent electrocatalysts in situ decorated on Ni foam for overall water splitting

Bifunctional NiCoP/NiCo Electrocatalysts on Nickel Foam for Overall Water Spillting

Dual-Functional Starfish-like P-Doped Co-Ni-S Nanosheets Supported on Nickel Foams with Enhanced Electrochemical Performance and Excellent Stability for Overall Water Splitting

Synthesis of nanoflower-like NF@MoSCo/Co2P composites for overall seawater splitting

Mo-doped NiCoP nanowire array grown in situ on Ni foam as a high-performance bifunctional electrocatalyst for overall water splitting

CoP Microscale Prism-like Superstructure Arrays on Ni Foam as an Efficient Bifunctional Electrocatalyst for Overall Water Splitting

Fast synthesis of nickel phosphide nanosheets for ultra-stable hydrogen evolution in seawater splitting

Preparation of Co(OH)2@NiFe/NF bifunctional electrocatalyst by electrodeposition for efficient water splitting

Ni-doped CoFeP As High-Efficeint Electrocatalysts for Water-Splitting

Interface engineered Co2P/CoMoP2 heterojunction with greatly improved electrocatalytic activity in water/seawater splitting

Anchoring Ni2P Sheets on NiCo2O4 Nanocone Arrays as Optimized Bifunctional Electrocatalyst for Water Splitting

Hydrothermal Prepared Bramble-like Double Arrays NiCo 2 S 4 Bifunctional Electrocatalysts for High-Efficiency Water Splitting

A NiCo2O4 Shell on a Hollow Ni Nanorod Array Core for Water Splitting with Enhanced Electrocatalytic Performance

Heterointerface Engineering of Ni 2 P–Co 2 P Nanoframes for Efficient Water Splitting

Hierarchical core-shell structural Ni2P/NiMoO4 @CoP/FeP2 nanorods as difunctional electrocatalysts for efficient overall water splitting

Enhanced Full-Seawater Splitting with CoNiP@N, P-C Core-Shell Electrocatalyst

Three-Dimensional Heterostructured NiCoP@NiMn-Layered Double Hydroxide Arrays Supported on Ni Foam as a Bifunctional Electrocatalyst for Overall Water Splitting

NiO/Co2P Nanosheets with Heterogeneous Structure as a Multifunctional Catalyst for Overall Water Splitting

Cu-Co-M arrays on Ni foam as monolithic structured catalysts for water splitting: effects of co-doped S-P

In-situ porous flake heterostructured NiCoP/Ni foam as electrocatalyst for hydrogen evolution reaction